Low foaming acidic degreasing agent(LFADAs) were prepared by blending sorbitol, n-octanoic acid, MJU-100A, Tetronix T-701, Na-dioctyl sulfosuccinate, Demol C, and phosphoric acid. The physical properties of LFADAs tested with aluminum specimen showed the following results ; when 3wt% LFADA-6 was performed at 70℃, the degreasing rate was 95% which is comparitively good, and the percentage of etching was 0.275% which was found to be less than that of commercialized product. When 20wt% of LFADA-6 was added at 65℃, the percentage of derusting was 92% and the good defoaming effect proved by following low foaming power tests respectively : Ross and Miles, and Ross and Clark methods.

Spin finish(NSFs) for synthetic fiber were prepared. NSF-3 was proved to be the best spin finish by testing the properties and emulsion stability, etc. of NSFs. NSF-3 prepared by blending of spindle oil 70g, paraffin wax 10g, glyceryl mono-oleate 5g, POE(10) nonylphenyl ether 4g, POE(20) sorbitan tri-oleate 4g, Na-dioctyl sulfosuccinate 4g, antistatic agent 2g and water 1g was excellent in its characteristics. Optimum physical conditions of nylon filament treated with NSF-3 according to the number of revolution of oil roller were obtained at conditions of 5.5rpm in the number of revolution of oil roller, 1.21% of oil pick up, and denier 69.2D.