This study investigates the effect of thermo-mechanical treatment on the damping capacity of the Fe-20Mn-12Cr- 3Ni-3Si alloy with deformation induced martensite transformation. Dislocation, αʹ and ε-martensite are formed, and the grain size is refined by deformation and thermo-mechanical treatment. With an increasing number cycles in the thermo-mechanical treatment, the volume fraction of ε-martensite increases and then decreases, whereas dislocation and α'-martensite increases, and the grain size is refined. In thermo-mechanical treated specimens with five cycles, more than 10 % of the volume fraction of ε-martensite and less than 3 % of the volume fraction of αʹ-martensite are attained. Damping capacity decreases by thermomechanical treatment and with an increasing number of cycles of thermo-mechanical treatment, and this result shows an opposite tendency for general metal with deformation induced martensite transformation. The damping capacity of the thermomechanical treated damping alloy with deformation induced martensite transformation greatly affect the formation of dislocation, grain refining and α'-martensite and then ε-martensite formation by thermo-mechanical treatment.

This study was carried out to investigate the effect of W substitution on the precipitation behavior of χ and σ phases in super duplex stainless steel. The χ phase was precipitated at the interface of ferrite / austenite phases and inside the ferrite phase at the initial stage of aging. With an increase in the aging time, the volume fraction of the χ phase increased, and then decreased with the transformation from the χ phase to the σ phase. The σ phase was precipitated later than the χ phase, and the volume fraction of x phase increased with the increase in the aging time. The ferrite phase was decomposed into the new austenite (γ2) and σ phases by aging treatment. The decomposition of the ferrite phase into the γ2 and σ phases was retarded by W substitution for Mo. The volume fraction of the χ phase increased and that of the σ phase decreased due to W substitution. The χ and σ phases were intermetallic compounds, which had lower nickel concentration, and higher chromium, molybdenum, and tungsten concentrations. The χ phase has higher molybdenum and tungsten concentrations than those of the σ phase. The amounts of chromium and nickel in the χ and σ phases did not change, but these phases have higher concentrations of molybdenum and tungsten due to W substitution for Mo.