This study examines the effects of the TiO2 content and TiO2 position in the core or shell within tubular carbon nanofibers on the photocatalytic activity under visible light. Core–shell tubular carbon nanofiber composites whose cores are filled with TiO2 nanoparticles (PMTi(10)P) are fabricated through coaxial electrospinning and subsequent heat treatment. The PMTi(10)P composites with well-preserved TiO2 nanoparticles in the core part induce more oxygen vacancies, Ti3+ species, chemisorbed oxygen species, and anatase phases, significantly improving the photocatalytic performance. They act as photoelectron traps, allowing more photoelectrons and holes to participate in the photocatalytic reaction and extending the absorbance of TiO2 to the visible light region. The resulting PMTi(10)P photocatalyst exhibits excellent performance of 100% removal of methylene blue within 30 min and maintains nearly 100% removal of 15 ppm methylene blue over 10 regeneration cycles, indicating consistent and stable photocatalytic performance.
This study demonstrates that low processing rate for producing polyacrylonitrile (PAN)-based carbon fiber is a critical to obtain a homogeneous radial microstructure with high resistance to oxidation, thereby resulting in their improved mechanical strength. The dry-jet wet spun PAN organic fibers were processed (e.g., stabilized and then carbonized) utilizing two different rates; one is 1.6 times longer than the other. The effect of processing rate on the microstructural evolutions of carbon fibers was analyzed by scanning electron microscopy after slow etching in air, as well as Raman mapping after graphitization. The rapidly processed fiber exhibited the multilayered radial structure, which is caused by the radial direction stretching of the extrusion in the spinning. In case of the slowly processed fiber, the layered radial structure formed in the spinning process was changed into a more homogeneous radial microstructure. The slowly processed fibers showed higher oxidation resistance, higher mechanical properties, and higher crystallinity than the rapidly processed one. Raman mapping confirmed that the microstructure developed during spinning was sustained even though fiber was thermally treated up to 2800 °C.