Activated carbon has broad application prospects for treating pollutants due to its easy availability, low cost and good adsorption. In our work, nano-activated carbons (NAC) with abundant functional groups are obtained by the oxidation modification of HNO3, ( NH4)2S2O8, and KMnO4, which are used to construct the particle electrodes to degrade NDEA in a continuous flow electrochemical reactor, and the influence of relevant factors on the performance of NDEA removal is discussed. The experimental data show that the optimal degradation efficiency is 42.55% at the conditions of 3 mL/min influent water flow, 0.21 M electrolyte concentration, 10 mA/cm2 current density, and 10 μg/mL initial NDEA concentration. The degradation of NDEA conforms to a quasi second order kinetic equation. The electrocatalytic mechanism of NAC electrodes for removing NDEA is firstly discussed. The effects of different free radicals on the degradation of NDEA are also demonstrated through free radical quenching experiments, indicating that the degradation of NDEA is dominated by ⋅OH. The degradation pathway of NDEA and final products are obtained using GC–MS. NAC particle electrodes as the cheap and efficient electrocatalyst in continuous flow electrochemical reactor system provide a greener solution for the removal of disinfection by-products from drinking water.

Carbon nanotube fiber is a promising material in electrical and electronic applications, such as, wires, cables, batteries, and supercapacitors. But the problem of joining carbon nanotube fiber is a main obstacle for its practical development. Since the traditional joining methods are unsuitable because of low efficiency or damage to the fiber structure, new methods are urgently required. In this study, the joining between carbon nanotube fiber was realized by deposited nickel–copper doublelayer metal via a meniscus-confined localized electrochemical deposition process. The microstructures of the double-layer metal joints under different deposition voltages were observed and studied. It turned out that a complete and defect-free joint could be fabricated under a suitable voltage of 5.25 V. The images of the joint cross section and interface between deposited metal and fiber indicated that the fiber structure remained unaffected by the deposited metal, and the introduction of nickel improved interface bonding of double-layer metal joint with fiber than copper joint. The electrical and mechanical properties of the joined fibers under different deposition voltages were studied. The results show that the introduction of nickel significantly improved the electrical and mechanical properties of the joined fiber. Under a suitable deposition voltage, the resistance of the joined fiber was 37.7% of the original fiber, and the bearing capacity of the joined fiber was no less than the original fiber. Under optimized condition, the fracture mode of the joined fibers was plastic fiber fracture.