In this work, effect of various process-control agents (PCAs) on the mechanical alloying of amorphous alloy of has been investigated. The dependence of the particle shape, size and crystallization behavior of the amorphous alloy powders on the type of PCAs and their concentrations was investigated by using X-ray diffraction, field-emission scanning electron microscopy and differential scanning calorimetry. It was found that the additive of toluene could affect positively the amorphization and thermally induced crystallization processes, as well as the size refinement, morphology and particle-size distribution of as-milled powders in comparison with alloy obtained without PCA.

TiCuNiAl quaternary amorphous alloy was prepared by high-energy ball milling process. A complete amorphization was confirmed for the composition of TiCuNiAl after milling for 30hrs. Differential scanning calorimetry showed a large super-cooled liquid region (T = T T, T and T: glass transition and crystallization onset temperatures, respectively) of 80 K. Prepared amorphous powders of TiCuNiAl were consolidated by spark-plasma sintering. Densification behavior and microstructure changes were investigated. Samples sintered at higher temperature of 713 K had a nearly full density. With increasing the sintering temperature, the compressive strength increased to fracture strength of 756 MPa in the case of sintering at 733 K, which showed a 'transparticle' fracture. The samples sintered at above 693 K showed the elongation maximum above 2%.