Supercross-linked polymers are widely used as carbon precursor materials due to their abundant carbon sources and low cost. In this paper, a supercross-linked polymer was prepared by the solvothermal method. The supercross-linked polymer as a precursor and the PPyC-800-A was synthesized by activating this with KOH. The microstructure, structure, and electrochemical performances of porous carbon PPyC-800-A were studied at different of temperature and carbon alkali ratio. According to the results, the porous carbon PPyC-800-1:2 is mainly composed of a stack of spherical particles with a high surface area of 1427.03 m2 g− 1, an average pore diameter of 2.32 nm, and a high specific capacitance of 217.7 F g− 1 at a current density of 1.0 A g− 1 in a 6 M KOH electrolyte. It’s retention rate is 97.58% after 5000 constant current charges and discharges. With a specific capacitance decay rate of 21.91 percent, an energy density of 11.96 Wh kg− 1, and a power density of 500.0 W kg− 1, the current density rises from 1.0 A g− 1 to 10.0 A g− 1, exhibiting remarkable electrochemical properties, cycling stability, and energy production performance This study contributes experimental ideas to the field of supercrosslinked polymer-derived carbon materials and energy storage.

Hypercrosslinked polymers HCPs have been widely used as precursors to prepare porous carbon materials because of their highly ordered porous structure and large specific surface area. In this paper, we used a solvothermal method to prepare a hypercrosslinked polymer, and the HCPC-700-A was prepared using an activation method with the hypercrosslinked polymer as the precursor. The effects of different carbon–alkali ratios on the microstructure, composition and electrochemical properties of porous carbon HCP were studied. The results show that the surface of porous carbon HCPC-700-A presents a relatively regular geometric shape, and a large number of pore structures are mainly micro- and mesopores. The specific surface area is 2074.53 m2 g− 1, and the average pore size is between 1.29 and 1.93 nm. Porous carbon HCPC-700-1:2 has excellent electrochemical performance in 1 M H2SO4, and the specific capacitance is up to 464.4 F g− 1 at a current density of 1 A g− 1. The specific capacitance decay rate is 29.72% when the current density is increased from 1 A g− 1 to 8 A g− 1. After 5000 cycles, the capacitance retention rate is 91.16% at a current density of 2 A g− 1, showing excellent electrochemical performance, good cycle stability and perfect energy storage performance. This research provides new experimental ideas for HCPs in the electrochemical energy storage field.

Metal–organic frameworks (MOFs) are network-like frameworks composed of transition metals and organic ligands containing oxygen or nitrogen. Because of its highly controllable composition and ordered porous structure, it has broad application prospects in the field of material synthesis. In this work, Zn4( PYDC)4(DMF)2∙3DMF (ZPD) was synthesized via a hydrothermal method. Self-doped nitrogen porous carbon ZPDC-T was then prepared by one-step carbonization. The results show that the self-doped nitrogen porous carbon ZPDC-850 has a micro/mesoporous structure with a specific surface area of 1520 m2 g− 1 and a nitrogen content of 6.47%. When a current density is 1.0 A g− 1, its specific capacitance is 265.1 F g− 1. After 5000 times of constant current charging and discharging, the capacitance retention rate was 79.2%. Thus, self-doped nitrogen porous carbon ZPDC-850 exhibits excellent electrochemical properties and good cyclic stability. Therefore, the self-doped nitrogen porous carbon derived from MOFs can be a promising electrode material for supercapacitors.