At high temperatures, molten salt has heat transfer properties like water. Molten salt has the characteristics of a strong natural circulation tendency, large heat capacity, and low thermal conductivity. Unlike sodium, molten salt does not react explosively exothermically with air. However, molten salt has a strong tendency to corrode materials, and its properties are easily changed by a sensitive reaction to oxygen and moisture. Therefore, it is necessary to study material corrosion properties and chemical control methods for nuclear fuel salts, which are eutectic mixtures. In this study, the optimal operation method of the thermal convection loop is established to perform the experiments on the molten salt. The process describes briefly as follows. The operation step consists of preparation, purification, transportation, and operation. In the preparation, the step checks the entire structure and equipment (TC, blower, vacuum pump, etc.). And melt the salt mixture at a high temperature (670°C) slowly in the purification step. Before injecting the molten salt, the surface temperature of the entire loop must retain temperature (about 500°C) constantly. Completely melted molten salt in the melting pot is flow along the pipe of the thermal convection loop in the transportation step. Lastly, the convection of molten salt goes to keep by the temperature difference. The thermal convection loop can be utilized for various experiments such as corrosion tests, component analyses, chemistry control, etc.

Molten salt used in the multipurpose molten salt experiment must be of high purity. Depending on the purpose of the experiment, only the base component of the molten salt be used, or a component simulating a nuclear fission product be added to the base component and used. In all cases, an increase in the concentration of impurities such as oxygen and moisture may lead to an erroneous interpretation when analyzing the experimental results. Therefore, molten salt should be purified before use. In this study, the purification of molten salt is described for multi-purpose molten salt experiments. The salt mixture is selected as MgCl2-NaCl and is quantified at a mixing ratio of 43mol%:57mol%. The salt mixture is treated in a glove box environment because of must minimize the reaction of adsorbing oxygen and moisture when the salt mixture is exposed to the atmosphere. MgCl2 is more likely to contain water than NaCl, the purification of the NaCl-MgCl2 mixture is established according to the purification process for removing water from MgCl2. A process for purifying the salt mixture briefly consists as follows: drying moisture, melting salts, purification, removing HCl, and stabilization. Through the process be able to obtain high-purity molten salt and more accurate experiment results.