A hierarchical pore structured novolac-type phenol based-activated carbon with micropores and mesopores was fabricated. Physical activation using a sacrificialsilicon dioxide (SiO2) template and chemical activation using potassium hydroxide (KOH) were employed to pre-pare these materials. The morphology of the well-developed pore structure was character-ized using field-emissionscanning electron microscopy. The novolac-type phenol-based activated carbon retained hierarchical pores (micropores and mesopores); it exhibited high Brunauer-Emmett-Teller specificsurface areas and hierarchical pore size distributions. The hierarchical pore novolac-type phenol-based activated carbon was used as an electrode in electric double-layer capacitors, and the specificcapacitance and the retained capacitance ratio were measured. The specificcapacitances and the retained capacitance ratio were en-hanced, depending on the SiO2 concentration in the material. This result is attributed to the hierarchical pore structure of the novolac-type phenol-based activated carbon.