The phase Ti-Nb-Sn-HA bio materials were successfully fabricated by high energy mechanical milling and pulse current activated sintering (PCAS). Ti-6Al-4V ELI alloy has been widely used as biomaterial. But the Al has been inducing Alzheimer disease and V is classified as toxic element. In this study, ultra fine sized Ti-Nb-Sn-HA powder was produced by high energy mechanical milling machine. The phase Ti-Nb-Sn-HA powders were obtained after 12hr milling from phase. And ultra fine grain sized Ti-Nb-Sn-HA composites could be fabricated using PCAS without grain growth. After sintering, the microstructures and phase-transformation of Ti-Nb-Sn-HA biomaterials were analyzed by scanning electron microscope (SEM) and X-ray diffraction (XRD). The relative density was obtained by Archimedes principle and the hardness was measured by Vickers hardness tester. The -Ti phase was obtained after 12h milling. As result of hardness and relative density, 12h milled Ti-Nb-Sn-HA composite has the highest values.

본 논문에서는 Telos Device를 이용한 검사 시 인가한 daN 힘의 차이와 무릎의 안정성에 관여하는 근육들의 개인차에 따른 전방십자인대의 동요 정도에 대해 연구하고자 한다. Telos Device를 이용한 Lachman Test로 검사하였으며, 오른쪽과 왼쪽을 각각 0, 15, 30 daN, 운동부하 후 30 daN의 힘으로 변화하며 검사하여 전방십자인대의 변화를 측정하였다. 근육량 측정은 CT(Computed Tom ography)를 이용하였으며, 힘줄(tendon)을 피해 근육을 측정하기 위해 무릎뼈(patella) 상방 8 cm의 위치를 검사하였다. 전방십자인대(Anterior Cruciate Ligament)의 변화 정도는 Piview의 Caliper 기능을 이용하여 측정 하였으며, 근육량은 CT 단면 영상을 Image J 프로그램을 이용하여 지방을 제외한 뼈와 근육의 면적을 측정 하였다. 측정값들은 SPSS Ver. 18을 이용하여 결과 값을 얻었다. Telos Device 로 인가하는 힘의 변화에 따라 전방십자인대의 동요 정도를 측정한 결과 오른쪽과 왼쪽 모두 15 daN 과 30 daN의 힘을 인가하였을 때 통계적으로 유의한 무릎 동요의 차가 발생하였으며(p<0.05), 30 daN 과 운동부하 후 30 daN 에서의 동요 정도는 유의한 차이를 보이지 않았다(p>0.05). 근육면적의 차이와 전방십자인대의 동요 정도와의 상관관계에서 15 daN의 압력에서 오른쪽 r=-0.45, 왼쪽 r=0.44로 음의 상관관계를 보였다(p<0.05). Telos Device에 인가 하는 힘의 정도에 따라 전방십자인대의 동요는 커지는 것으로 분석되며, 또한 개인의 근육량의 차이에 따라 전방십자인대의 동요 정도에도 차이를 보이는 것으로 분석된다. 따라서 개인의 근육량의 차이에 따라 Telos Device에 인가되는 힘도 변화되어야 하는 것으로 사료된다.