β-Resin was extracted by solvent separation of refined coal tar pitch. Several analytical methods revealed that β-resin had a better aromatic plane packing structure and a higher number of carbon residues, making it ideal for mesophase transformation. The mesophase transformation process of β-resin (the formation of liquid-crystalline spheres, the growth of mesophase spheres, and the coalescence and disintegration of mesophase spheres) was observed in situ using a polarizing microscope with a hot stage. Moreover, the mesophase transformation mechanism of β-resin was investigated at each transformation stage. The mesophase content and mesophase transformation kinetics were analyzed based on the area method and quinoline insoluble (QI) substitution method. Both methods revealed changes in the mesophase content of β-resin. However, the test results of the two methods were slightly different at the initial stage of mesophase transformation and tended to be consistent during the later stage.

Heteroatoms in situ-doped hierarchical porous hollow-activated carbons (HPHACs) have been prepared innovatively by pyrolyzation of setaria viridis combined with alkaline activation for the first time. The micro-morphology, pore structure, chemical compositions, and electrochemical properties are researched in detail. The obtained HPHACs are served as outstanding electrode materials in electrochemical energy storage ascribe to the particular hierarchical porous and hollow structure, and the precursor setaria viridis is advantage of eco-friendly as well as cost-effective. Electrochemical measurement results of the HPHACs electrodes exhibit not only high specific capacitance of 350 F g−1 at 0.2 A g−1, and impressive surface specific capacitance (Cs) of 49.9 μF cm−2, but also substantial rate capability of 68% retention (238 F g−1 at 10 A g−1) and good cycle stability with 99% retention over 5000 cycles at 5 A g−1 in 6 M KOH. Besides, the symmetrical supercapacitor device based on the HPHACs electrodes exhibits excellent energy density of 49.5 Wh kg−1 at power density of 175 W kg−1, but still maintains favorable energy density of 32.0 Wh kg−1 at current density of 1 A g−1 in 1-ethy-3-methylimidazolium tetrafluoroborate ( EMIMBF4) ionic liquid electrolyte, and the excellent cycle stability behaviour shows the nearly 97% ratio capacitance retention of the initial capacitance after 10,000 cycles at current density of 2 A g−1. Overall, the results indicate that HPHACs derived from setaria viridis have appealing electrochemical performances thus are promising electrode materials for supercapacitor devices and large-scale applications.