Fe3O4/g-C3N4/TiO2 catalyst has been fabricated using a simple ultrasonic method with high photocatalytic activity. The morphology, structure and optical properties of Fe3O4/ g-C3N4/TiO2 were systematically investigated by a variety of characterization techniques. The optimum degradation conditions were investigated by degrading tetracycline (TC) under visible light irradiation. The results showed that the degradation efficiency was the highest when the initial TC concentration was 5.0 mg/L, the pH value was 11 and the catalyst dosage was 1.0 g/L. After 100 min of visible light irradiation, the degradation efficiency of TC achieved at 73.61%, which was 1.64 and 1.19 times that of g-C3N4 and Fe3O4/ g-C3N4, respectively. Moreover, Fe3O4/ g-C3N4/TiO2 had good stability and recyclability. The results of capture experiments showed that ‧O2 − and ‧OH were the main active species during the photocatalytic process, and a possible photocatalytic reaction mechanism of Fe3O4/ g-C3N4/TiO2 catalyst was proposed. This study provides a new way to improve the photocatalytic performance of g-C3N4, which has great potential in degrading pollutants such as antibiotics in wastewater.

Graphene-derived materials are an excellent electrode for electrochemical detection of heavy metals. In this study, a MnO2/ graphene supported on Ni foam electrode was prepared via ultrasonic impregnation and electrochemical deposition. The resulting electrode was used to detect Pb(II) in the aquatic environment. The graphene and MnO2 deposited on the Ni foam not only improved active surface area, but also promoted the electron transfer. The electrochemical performance towards Pb(II) was evaluated by cyclic voltammetry (CV) and square wave anodic stripping voltammetry (SWASV). The prepared electrode exhibited lower limit of detection (LOD, 0.2 μM (S/N = 3)) and good sensitivity (59.9 μAμM−1) for Pb(II) detection. Moreover, the prepared electrodes showed good stability and reproducibility. This excellent performance can be attributed to the strong adhesion force between graphene and MnO2, which provides compact structures for the enhancement of the mechanical stability. Thus, these combined results provide some technical considerations and scientific insights for the detection of heavy metal ions using composite electrodes.