In2O3 doped WO3 powders were prepared by a polymer solution route and their NO2 gas sensing properties were analyzed. The synthesized powders showed nano-sized particles with specific surface areas of 6.01~21.5 m2/g and the particle size and shape changed according to the content of In2O3. The gas sensors fabricated with the synthesized powders were tested at operating temperatures of 400~500 oC and 100~500 ppm concentrations of NO2 atmosphere. The particle size and In2O3 content affected on the initial sensor resistance in an air atmosphere. The highest sensitivity (8.57 at 500 oC), which was 1.77 higher than the sensor consisting of the pure WO3 sample, was measured in the 0.5 mol% In2O3 doping sample. In addition, the response time and recovery time were improved by the addition of In2O3.

콘크리트 구조물의 내구성을 향상하기 위해 개발된 통기성이 개선된 나노합성 폴리머 표면처리제를 도포한 콘크리트의 내구성향 상 효과를 평가하기 위해 내부 구조와 공극량을 측정하였으며, 염분침투, 탄산화, 동결융해 및 화학적 침식 저항성에 대한 실험을 진행하여 기 존 표면처리제와 비교․분석하였다. 공극량과 내부 구조를 측정한 결과, 나노합성 폴리머 표면처리제를 도포한 콘크리트는 0.3㎛ 이상의 공극과 0.1㎛ 이하의 공극영역에서 세공량이 감소하는 경향을 보였으며, 전자현미경을 통한 촬영된 내부는 수화조직에 의해 치밀함을 보였다. 나노합 성 폴리머 표면처리제를 도포한 콘크리트의 염분침투 깊이는 무도포 콘크리트에 비해 약 92% 이상, 수성 에폭시 표면처리제를 도포한 콘크리 트보다도 약 70% 이상 감소하였다. 이는 탄산화, 동결융해 및 화학적 침식 저항성 실험에서도 비슷하게 나타났다. 특히 황산 5% 수용액에 침지 실험한 화학적 침식 저항성 실험에서는 침지 12일 이후 무도포 콘크리트와 수성 에폭시 표면처리제를 도포한 콘크리트에서 -4%의 중량감소를 보였지만, 나노합성 폴리머 표면처리제를 도포한 콘크리트는 -1.7%의 중량감소율을 보였으며, Tsivilis et al.에 의한 외관등급 조사법에서도 우 수한 결과를 보였다.