During the field operation of the Korean MBT(Main Battle Tank), the multi-smoke projectile launching system failed to function. As a result of conducting analysis, it was confirm that the gear shaft of reducer was failed. Therefore, a study on improvement in impact resistance of the reducer was conducted. The reducer was improved impact resistance by changing the design and material of gear shaft. The reliability of modified reducer was investigated by finite element analysis, performance and environmental tests. As a result of analysis, a strength of the modified gear shaft was improved by about 20 times than before improvement. The results of performance and environmental test show that the modified reducer is applicable for Korean MBT under the severe conditions. The quality improvement of multi-smoke projectile launching system contributes to survivability of Korean MBT.

탄소섬유는 경량이면서 높은 기계적 특성 때문에 우주항공, 선박, 자동차, 토목 및 건축과 같은 산업분야에서 그 어느 때 보다 더 광범위하게 적용되고 있다. 본 연구는 섬유혼입률 및 섬유길이 변화에 따른 탄소섬유 보강시멘트 복합재료( CFRC)의 역학적 특성과 휨 거동을 분석하였으며, 또한 자연 낙하시험에 의한 모르타르 시편에 대한 내충격성을 비교, 검토하였다. 더불어, 탄소섬유(CF)의 혼입률은 0.5%, 1.0%, 2.0% 및 3.0%로 변화를 주었으며, 각각의 섬유길이는 6 mm와 12 mm를 사용 하였다. 실험결과, 플로우 값은 탄소섬유의 뭉침현상으로 인해 유동성 측면에서 매우 불리하였으며, 단위용적질량은 다소 감소하였다. 특히, 압축강도는 탄소섬유 혼입량이 증가함에 따라 감소하는 것으로 나타내었다. 반면 휨 강도는 섬유 길이가 12 mm이고 2% 혼입한 것이 가장 높은 휨 강도를 보였다. 내충격성 시험결과, 보통 모르타르 시편은 완전파괴까지의 낙하횟수가 2∼3회 정도 걸리지만 반면 CFRC 시편은 섬유혼입량이 증가함에 따라 다소 차이가 있지만, 섬유길이가 12 mm이고 섬유혼입량 2% 인 경우 충격에 대한 저항성이 가장 높았다.

In this study, impact performance of steel fiber-reinforced concrete was evaluated using existing impact formulae. The existing formulae were evaluated as to whether they can predict impact performance of steel fiber-reinforced concrete well.