PURPOSES: To characterize the aging effect on asphalt binder, dynamic shear modulus mastercurve of two typical asphalt binders are developed. METHODS: To develop dynamic shear modulus mastercurve, dynamic shear modulus at high temperature and creep stiffness at low temperature are measured by temperature sweep test and bending beam rheometer test, respectively. RESULTS: It is observed that the aging effect on asphalt binder can be clearly observed from dynamic shear modulus mastercurve and the mastercurve can be utilized to predict behavior of asphalt binder at wide range of temperature. CONCLUSIONS: It is confirmed that SBS 5% modified binder has more desirable mechanical property at low and high temperature as a pavement material comparing to PG64-22 binder and the mastercurve is an effective tool to evaluate the property of asphalt binder.
본 연구에서는 국내에서 사용되고 있는 우레탄계, 세라믹계, 폴리실록산계 및 불소수지계 강교량용 도장계를 대상으로 실내 부식실험을 실시하여 도장계별 노화모델을 도출하였다. 상도를 구분하여 각 도장계별로 시험편을 제작하였으며, 직경 0.5, 1, 3, 5 mm의 원형 결함을 도입하였다. ISO 20340를 이용하여 극한환경을 모사한 부식촉진실험을 실시하였다. 도장계별 노화곡선은 원형결함의 노화면적을 기준으로 평가되었다. 노화곡선을 사용하여 공용중인 강교의 도장 사용수명을 평가하기 위하여 촉진배율을 산출하였으며, 촉진배율은 ISO 20340과 ISO 9223의 대기환경 부식속도를 기준으로 산출되었다. 실험결과, 노화진전속도는 원형결함의 크기와 상관없이 증가하였으며, 노화면적이 3%일 때 우레탄 도장계의 노화수명은 C2, C3, C4 및 C5 등급에서 약 31.8, 15.8, 9.9 및 3.9년으로 평가되었다.
Painting system are widely used to prevent corrosion damage The coating method on various corrosion preventive method was usually adopted for the functional ability and excellent appearance. In this study, to evaluate the deterioration curve of coating system for steel bridge, the combined cyclic corrosion test was conducted base on ISO 20340. The deterioration areas were measured depending on corrosion cycle. The deteriorations of newly-built coating were compared with those of re-coating.