High-temperature oxidation of a Ni-based superalloy was analyzed with samples taken from gas turbine blades, where the samples were heat-treated and thermally exposed. The effect of Cr/Ti/Al elements in the alloy on high temperature oxidation was investigated using an optical microscope, SEM/EDS, and TEM. A high-Cr/high-Ti oxide layer was formed on the blade surface under the heat-treated state considered to be the initial stage of high-temperature oxidation. In addition, a PFZ (γ’ precipitate free zone) accompanied by Cr carbide of Cr23C6 and high Cr-Co phase as a kind of TCP precipitation was formed under the surface layer. Pits of several μm depth containing high-Al content oxide was observed at the boundary between the oxide layer and PFZ. However, high temperature oxidation formed on the thermally exposed blade surface consisted of the following steps: ① Ti-oxide formation in the center of the oxide layer, ② Cr-oxide formation surrounding the inner oxide layer, and ③ Al-oxide formation in the pits directly under the Cr oxide layer. It is estimated that the Cr content of Ni-based superalloys improves the oxidation resistance of the alloy by forming dense oxide layer, but produced the σ or μ phase of TCP precipitation with the high-Cr component resulting in material brittleness.

본 실험은 붕어(Crucian carp, Carassius carassius)(무게 39.7±3.1 g, 전장 14.8±0.5 cm)의 수인 성 니켈 0, 10, 20, 40, 80 및 160 mg Ni2+/l 농도로 96시간 급성 노출을 실시하였다. 수인성 니 켈에 노출된 붕어의 반수치사농도(LC50)는 117.69 mg Ni2+/l으로 나타났다. 혈액학적 성상에서 RBC count는 수인성 니켈 96시간 급성 노출 중 48시간에서 유의적으로 증가한 반면, 96시간에 서 유의적 감소가 나타났다. MCV와 MCH는 96시간에서 80 mg Ni2+/l 농도에서 유의적으로 증 가했다. Calcium, magnesium, glucose, cholesterol, total protein, AST, ALT 및 ALP 와 같은 혈장 성분은 수인성 니켈 노출에 의해 유의적 변화가 나타났다. 이 연구의 결과는 수인성 니켈 노출 에 따른 붕어의 생존율, 혈액학적 성상 및 혈장 성분의 변화를 확인하고 이는 수인성 니켈의 독성에 의한 것으로 판단했다.