        1.
        2022.11 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        For the selective catalytic reduction of NOx with ammonia (NH3-SCR), a V2O5WO3/TiO2 (VW/nTi) catalyst was prepared using V2O5 and WO3 on a nanodispersed TiO2 (nTi) support by simple impregnation process. The nTi support was dispersed for 0~3 hrs under controlled bead-milling in ethanol. The average particle size (D50) of nTi was reduced from 582 nm to 93 nm depending on the milling time. The NOx activity of these catalysts with maximum temperature shift was influenced by the dispersion of the TiO2. For the V0.5W2/nTi-0h catalyst, prepared with 582 nm nTi-0h before milling, the decomposition temperature with over 94 % NOx conversion had a narrow temperature window, within the range of 365-391 °C. Similarly, the V0.5W2/nTi-2h catalyst, prepared with 107 nm nTi-2h bead-milled for 2hrs, showed a broad temperature window in the range of 358~450 °C. However, the V0.5W2/Ti catalyst (D50 = 2.4 μm, aqueous, without milling) was observed at 325-385 °C. Our results could pave the way for the production of effective NOx decomposition catalysts with a higher temperature range. This approach is also better at facilitating the dispersion on the support material. NH3-TPD, H2-TPR, FT-IR, and XPS were used to investigate the role of nTi in the DeNOx catalyst.
        4,300원
        3.
        2015.06 KCI 등재 구독 인증기관 무료, 개인회원 유료
        본 연구는 폴리프로필렌(PP) 수지의 Co 및 Mo 촉매에 의한 반응시간과 농도변화에 따른 저온열분해 액화특성을 파악하고자 회분식 반응기를 이용하여 특정 온도(425, 450, 475℃)에서의 전환율을 측정하였다. 열분해 시간은 20~80분으로 설정하였고 생성물은 산업통상자원부에서 고시한 증류성상 온도에 따라 가스, 가솔린, 등유, 경유, 중유로 분류하였다. 그리고 450℃ 반응온도에서 촉매 사용에 따른 전환율은 모든 반응시간에 있어 Mo 촉매 > Co 촉매 > 무촉매 순이었다. Co 및 Mo 촉매 농도별 PP 전환율 및 열분해 생성물 수율은 Co:Mo=50:50 혼합시 가장 우수한 것으로 나타났다.
        4,000원