심부 처분환경조건에서 붕규산유리고화체의 장기침출거동을 규명하기 위하여 3종의 모의붕규산유리고화체에 대한 장기침출실험이 1997년에 착수되었다. 5년간의 침출결과는 붕소가 본 붕규산유리고화체의 장기침출지표물질로 사용될 수 있음을 확인시켜 주었고, 비록 고화체들의 조성은 약간씩 다르지만, 초기 1년여 기간동안의 침출률을 제외한 장기침출률은 S/V에도 무관하게 0.03g/-day 에 근접하는 경향을 보여주고 있다.
This research is to investigate the effect of borosilicate glass powder on neutron shielding capability of cement mortar. The average particle size of the borosilicate glass powder was 13 μm. It was found that the addition of borosilicate glass powder increased 28 day compressive strength. In addition, neutron shielding capability of cement mortar also increased by the addition of borosilicate glass powder. Considering our earlier findings on enhanced thermal neutron shielding of cement mortar by borosilicate glass powder, the use of borosilicate glass powder was found to be effective to shield neutron when the cement mortar was exposed to the neutron radiation. It can be concluded that borosilicate glass powder is a good alternative material for neutron shielding purposes.
핵폐기물을 고화시키는 재료로 사용하는 붕규산염(borosilicate) 유리의 용해는 지층 처분장에 처리된 고준위 방사성 폐기물의 생태계 유출을 결정할 수 있는 중요한 화학반응이다. 습식 실험에서 유리의 용해속도(dissolution rate)는 유리 화학조성에 의해 크게 좌우되는 것이 관찰된다. 유리의 bulk 구조를 규명한 분광분석 실험에 의하면 유리의 화학조성과 분자수준(molecular-level) 구조(예: SiO4 사면체의 연결구조와 B 원소의 배위구조) 사이의 상관관계가 존재한다. 따라서 화학조성에 따른 유리 용해도의 차이는 조성에 따른 bulk 내부구조의 변화로 이해되어 왔다. 그런데 유리 표면은 수용액과 계면을 이루면서 용해 과정에서 가장 직접적으로 반응하는 부분이기 때문에, 화학조성에 따른 표면구조 변화에 대한 지식 또한 필요하다. 본 논문에서는 분자 동역학(molecular dynamics, MD) 시뮬레이션을 사용하여 4가지의 다른 화학조성을 가지는 소듐붕규산염 유리(xNa2O·B2O3·ySiO2 화학조성)에 대하여 bulk 구조와 실험으로 얻기 어려운 표면(surface) 구조를 연구하였다. MD 시뮬레이션은 유리 표면의 화학조성과 분자수준 구조가 bulk의 것과 매우 상이한 결과를 보여준다. 본 연구의 MD 시뮬레이션 결과는 화학조성에 따른 유리 용해도(특히 초기 용해과정)는 bulk 구조의 변화보다 유리 표면구조의 변화에 의해 크게 좌우될 수 있다는 표면구조에 대한 이해의 중요성을 역설한다.