        1.
        2017.04 서비스 종료(열람 제한)
        The effect of loading on chloride penetration into concrete is evaluated in this study. It is found that the chloride pene- tration rates for OPC concrete and blast furnace slag BFS concrete under the tensile stress were increased by 29% and 77%, respectively. The diffusion coefficient of FA and BFS concrete was lower than that of conventional concrete without BFS, no loads and stress states. Under tensile stress, the diffusion coefficient for FA and BFS, plain concrete showed higher values with increasing stress. The influence of specific surface area on the diffusion coefficient was investigated. As a result, the larger the specific surface areas of BFS are the lower diffusion coefficients. This tendency was more pronounced under the high stress conditions. The chloride penetration depth was distributed uni- formly when no stress was applied. However, in the case of tensile loading, the diffusion depth was not distributed uni- formly, and showed prominent characteristics. This result indicates that analysis using average values of chloride pene- tration depth is not proper under load conditions.
        2.
        2015.04 서비스 종료(열람 제한)
        As a result of strength test on FA and BFS, FA concrete showed higher increase of strength compared to OPC, when FA4000 and FA5000 were mixed 30%, respectively. For BFS concrete, those mixed with 30% and 50% of BFS8000, respectively, showed higher or equivalent strength compare to OPC. As a result of test of chloride penetration on FA and BFS, diffusion coefficients of concrete mixed with 30% FA4000 and FA5000, respectively, showed to restrain average 6.5% of diffusion coefficient compared to OPC. And in case of BFS concrete, those mixed with BFS6000 and BFS8000, restrained diffusion of chloride ions 253% and 336%, respectively, compared to OPC. Therefore, Mixing 50% of BFS was most efficient in order to maximize restraint of chloride penetration according to metathesis of large amount.
        3.
        2015.01 KCI 등재 서비스 종료(열람 제한)
        This study examined dynamic and characteristics and chloride penetration of concrete mixed with large amount of FA and BFS, which are considered for positive application to construction fields with purpose of long-tern durability of concrete structures. As a result of strength test on FA and BFS, FA concrete showed higher increase of strength compared to OPC, when FA4000 and FA5000 were mixed 30%, respectively. For BFS concrete, those mixed with 30% and 50% of BFS8000, respectively, showed higher or equivalent strength compare to OPC. As a result of test of chloride penetration on FA and BFS, diffusion coefficients of concrete mixed with 30% FA4000 and FA5000, respectively, showed to restrain average 6.5% of diffusion coefficient compared to OPC. And in case of BFS concrete, those mixed with BFS6000 and BFS8000, restrained diffusion of chloride ions 253% and 336%, respectively, compared to OPC. Therefore, Mixing 50% of BFS was most efficient in order to maximize restraint of chloride penetration according to metathesis of large amount. For relation between compression strength and diffusion coefficient of FA and BFS concrete, as strength increased, diffusion coefficient decreased. In this study, when mixing FA and BFS to concrete for long-run durability and restraint against chloride penetration, for FA, mixing it to concrete with less or equivalent 30% of replacement rate was most efficient. And for BFS, as fineness was higher and mixing it to concrete with less or equivalent 50% of replacement rate, there were results of higher strength compared to OPC and more efficient restraint of chloride ions.