Direct spring loaded pressure relief valve(DSLPRV) is a safety valve to relax surge pressure of the pipeline system. DSLPRV is one of widely used safety valves for its simplicity and efficiency. However, instability of the DSLPRV can caused by various reasons such as insufficient valve volume, natural vibration of the spring, etc. In order to improve reliability of DSLPRV, proper selection of design factors of DSLPRV is important. In this study, methodology for selecting design factors for DSLPRV was proposed. Dynamics of the DSLPRV disk was integrated into conventional 1D surge pressure analysis. Multi-objective genetic algorithm was also used to search optimum design factors for DSLPRV.

금속 유기 골격체(Metal Organic Framework, 이하 MOF) 종류의 하나인 제올라이트형 이미 다졸레이트 골격체(Zeolitic Imidazolate Framework, 이하 ZIF) 중 ZIF-8은 Zn 금속이온과 imidazole 유기 리간드의 결합으로 이루어져 있다. 본 연구에서는 여러 종류의 용매에서 합성된 ZIF-8의 1차 결정과 2차 입자의 형성이 용매가 가진 특성에 영향을 받는 것을 확인하였다. HBD(hydrogen bond donation) 값이 큰 용매에서 합성된 ZIF-8의 1차 결정은 HBD 값이 작은 용매에서의 것보다 크기가 컸고, 용매의 유전상수의 값이 작을수록 2차 입자의 크기가 큰 ZIF-8이 합성되었다.

물과 에탄올의 혼합용액에 HCI을 촉매로하여 금속알콕사이드의 가수분해로부터 코오디어라이트 분말을 제조하였다. 이때 HCI/precursor 몰비로써 촉매의 양을 조절하였다. 건조분말 중의 용매를 제거하기위해 800˚C에서 3시간 하소처리하였다. 이들 하소된 분말에 대하여 시차열분석과 X-선회절분석을 행한 결과-920˚C에서 μ-cordierite, -1030˚C에서 α-cordierite 결정상의 생성을 확인하였다. 또한, 하소분말을 가압성형한 후 1300˚C에서 4시간 열처리한 결과 HCI양에 따라 기공율 19.45-25.45%, 부피비중 2.06-1.70g/㎤, 유전상수 1.38-3.38 범위의 소결체를 얻었다. HCI양이 증가할수록 기공율은 증가한 반면에 비유전상수와 부피비중은 감소하였다.

In this study, an experimental research is conducted to determine the influence of field conditions on the soil dielectric constant in order to evaluate the feasibility of using TDR method as a cavity exploration. Dielectric constant of the ground considering field conditions(e.g. casing and ground disturbance) was measured using TDR method. The results conclude that the dielectric constant of ground tended to decrease with the increase in the water contents and density.