Much attention has been paid to thermally conductive materials for efficient heat dissipation of electronic devices to maintain their functionality and to support lifetime span. Hexagonal boron nitride (h-BN), which has a high thermal conductivity, is one of the most suitable materials for thermally conductive composites. In this study, we synthesize h-BN nanocrystals by pyrolysis of cost-effective precursors, boric acid, and melamine. Through pyrolysis at 900oC and subsequent annealing at 1500oC, h-BN nanoparticles with diameters of ~80 nm are synthesized. We demonstrate that the addition of small amounts of Eu-containing salts during the preparation of melamine borate precursors significantly enhanced the crystallinity of h-BN. In particular, addition of Eu assists the growth of h-BN nanoplatelets with diameters up to ~200 nm. Polymer composites containing both spherical Al2O3 (70 vol%) and Eu-doped h-BN nanoparticles (4 vol%) show an enhanced thermal conductivity (λ ~ 1.72W/mK), which is larger than the thermal conductivity of polymer composites containing spherical Al2O3 (70 vol%) as the sole fillers (λ ~ 1.48W/mK).
질화규소-질화붕소 복합재료의 접촉하중에 의한 손상거동을 질화붕소 첨가량의 함수로 고찰하였다. Indentation응력-변형율 곡선은 선형성을 벗어나 소성 특성을 갖는 재료임이 밝혀졌으며, 재료 표면으로 부터의 ring이나 cone형상의 균열 대신 표면하부에 전단응력에 의한 마이크로 크기의 준소성 변형 영역이 넓게 형성되어 손상저항성이 높은 재료로의 활용이 기대되었다. 이 때 마이크로 파괴와 연관된 shear faults가 이 재료의 소성을 갖도록 하는데 중요한 역할을 하였다. 질화붕소의 첨가량이 증가함에 따라 질화규소-질화붕소 재료는 보다 soft해지고 준소성의 특성을 나타내었다.