In this paper, a shot peening was conducted to improve fatigue life by increasing resistance to hydrogen embrittlement of STS316 steel, which is widely used in hydrogen environments. First, considering the efficiency of the shot peening process, an effective Almen intensity was selected and applied to the specimen surface. Second, the specimen was hydrogen embrittled at room temperature (25°C) and high temperature (60°C) using electrochemical hydrogen charging. Third, the mechanical property tests (tensile, hardness, roughness) and 4-points rotational bending fatigue tests of the specimen were performed. All mechanical properties decreased, but the fatigue life of the shot peened specimens improved at the both temperature conditions. Ultimately, the fatigue characteristics against hydrogen embrittlement of STS316 steel, which is used in various industrial fields, are improved through an effective shot peening process, and the effect is believed to be very significant.

본 연구에서는 피로 손상된 용접이음의 피로수명 향상을 위한 방법으로 햄머피닝 처리법의 적용성을 검토하기 위하여 면외거셋 필렛 용접이음과 하중비전달형 리브 필렛 용접이음의 피로실험을 실시하였다. 본 실험에서는 면외거셋과 리브를 필렛 용접한 후 햄머피닝 처리를 하지 않은 용접그대로의 시험편, 용접후 햄머피닝 처리한 시험편, 그리고 용접그대로 시험편의 피로수명의 50% 시점에 햄머피닝 처리를 한 시험편의 피로실험을 실시하였다. 그리고 햄머피닝 처리에 의한 면외거셋과 리브 용접토우부의 형상 및 표면응력의 변화를 측정하였다. 그 결과, 햄머피닝처리에 의해 30~83MPa의 압축잔류응력이 도입 되었으며, 이로 인하여 강구조물의 제작시 용접후에 햄머피닝 처리를 실시하면 피로수명을 크게 향상 시킬 수 있을 뿐만 아니라, 이를 공용기간이 예상 피로수명의 50% 이하인 강구조물의 용접이음에 적용하여도 최소 1.3배 이상의 피로수명과 피로한계 향상효과를 기대할 수 있음을 제시하였다.