        1.
        2019.02 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Glass wool is widely used as a typical soundproofing material because it has superior characteristics as a soundproofing material as well as excellent marketability. However, moisture penetration through condensation and cleaning up causes deterioration of insulation and soundproofing performance. In this study, we evaluate the wettability and sound absorption performance when the metal is deposited on the surface of glass wool. The performance is examined based on parameters such as the angle test, drying speed, the absorbency, the moisture content, the wettability. The wettability data shows that Cu coated glass wool is the best performance compaed to Ti coated one. The sound insulation characteristics are also compared by using the impedance tube. At the low frequency range, there is no difference among the test specimens, however, at the frequency above the 250 Hz range, Cu coating shows 10 % better in th sound asorption. Ti coating has almost same to the existing glasss wool performance. It turns out that metal coating on the glass wool seems to be very promising: the metal deposition reveals strong water repellency and sound absorption performance is equivalent to the existing glass wool.
        4,000원
        2.
        2019.02 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Glass wool is a fiber made by melting sand and waste glass at high temperature. It has been used as an inorganic fiber for sound absorption, insulation, and non-combustible materials for automobiles, ships, and household appliances. However, the disadvantage comes from the moisture penetration through condensation and cleaning up so that it deteriorates insulation and soundproofing performance. In order to overcome the disadvantages of glass wool, we investigate the water repellency by plating metal on the surface of glass wool with Cu and Ti while coating stability is considered. The thickness of the deposited metal is about 300 nm. The deposition chemicals and the image of the specimen are analyzed by using SEM equipment. The electron microscopic result shows that quite amount of Cu and Ti metals are deposited on the glass wool surface.
        4,000원