In this study, we have fabricated the phenolic resin (PR)/polyacrylonitrile (PAN) blend-derived core-sheath nanostructured carbon nanofibers (CNFs) via one-pot solution electrospinning. The obtained core-sheath nanostructured carbon nanofibers were further treated by mixed salt activation process to develop the activated porous CNFs (CNF-A). Compared to pure PAN-based CNFs, the activated PR/PAN blend with PR 20% (CNF28-A)-derived core-sheath nanostructured CNFs showed enhanced specific capacitance of ~ 223 F g− 1 under a three-electrode configuration. Besides, the assembled symmetric CNF28-A//CNF28-A device possessed a specific capacitance of 76.7 F g− 1 at a current density of 1 A g− 1 and exhibited good stability of 111% after 5,000 galvanostatic charge/discharge (GCD) cycles, which verifies the outstanding long-term cycle stability of the device. Moreover, the fabricated supercapacitor device delivered an energy density of 8.63 Wh kg− 1 at a power density of 450 W kg− 1.

In preparation of porous carbon materials microwave oven brightening is one of the warming modes used ever. The various procedures that take place in microwave combustion process include carbonization, incitation, and recovery and thus carbon is defined. This paper compares ideal conditions of traditional warming methods, as well as their implementation potential, losses, and specifications. This porous carbon with heat treatment possesses various properties and they are well suited for energy applications which require constrained space such as hydrogen storage in solid-state and supercapacitors. The enhanced properties are chemical and thermal stability, ready availability, low framework density and ease of processability. The recent trend in class of porous carbons is Activated Carbons that are employed traditionally as adsorbents or catalyst supporters but currently, they found potent applications in fabricating for hydrogen storage materials and supercapacitors. These activated carbons are much enhanced form in class of porous carbon materials and they possess the capability to enable hydrogen economy, where the energy carrier is hydrogen. Therefore, the utility of activated carbons as a source for energy storage experiences a rapid growth at current trend and they possess significant advances. This investigation is based on detailed cost development data and electrical imperativeness applications.

본 연구에서는 “이온젤” 이라고 불리는 고분자 기반의 PVA(polyvinyl alcohol) 기반의 고체 전 해질에 이온성 액체 BMIMBF4 (1-buthyl-3-methylimidazolium tetrafluoroborate)를 첨가하여 제조한 전 고체 전해질과 활성탄소와 금속유기골격체 복합재료 기반의 전극 재료를 이용하여 슈퍼커패시터를 제작 하였으며, 유기골격체의 유 무에 따른 전기화학적 특성을 분석하여 보았다. 슈퍼커패시터의 전기화학적 특 성은 순환전압전류법(CV), 전기화학적 임피던스 분광법(EIS) 및 전정류 충·방전법(GCD)을 통하여 비교 및 분석하여 보았다. 그 결과로, 금속유기골격체가 함유되지 않은 슈퍼커패시터의 전기용량값은 380 F/g 으로 확인 할 수 있었고, 이 값은 금속유기골격체를 첨가하였을 때 340 F/g로 감소하는 현상을 확인할 수 있었 다. 이러한 결과로 1 wt%의 금속유기골격체의 함유량은 전기화학적 특성 감소에 영향을 주는 것으로 사료 되며 이러한 결과를 바탕으로 금속유기골격체의 첨가량을 최적화 할 필요가 있다고 판단된다

Chlorella-derived activated carbon (CDAC) with a high specific surface area and hierarchical pore structure was prepared as a CO2 adsorbent and as a supercapacitor electrode material. During KOH activation of Chlorella-derived carbon, metallic K gas penetrated from the outer walls to the inner cells, and pores formed on the outer frame and the inner surface. Micropores were dominant in CDAC, contributing toward a high specific surface area (> 3500 m2/g) and a hierarchical pore structure owing to the cell walls. Consequently, CDAC exhibited a high CO2 adsorption capacity (13.41 mmol/g at 10 atm and room temperature) and afforded high specific capacitance (142 F/g) and rate capability (retention ratio: 91.5%) in supercapacitors. Compared with woody- and herbaceous-biomass-derived activated carbons, CDAC has a superior specific surface area when the precursors are used without any pretreatment under the same conditions due to their soft components such as lipids and proteins. Furthermore, developing microalgae into high-value-added products is beneficial from both economic and environmental perspectives.

Biochar obtained from the thermal conversion of biomass has high potential as a substitute material for activated carbon and other carbon-based materials because it is economical, environmentally friendly, and carbon-neutral. The physicochemical properties of biochar can also be controlled by a range of activation methods such as physical, chemical, and hydrothermal treatments. Activated biochar can be used as a catalyst for the catalytic pyrolysis of a biomass and as an absorbent for the removal of heavy metal ions and atmospheric pollutants. The applications of biochar are also expanding not only as a key component in producing energy storage materials, such as supercapacitors, lithium ion batteries, and fuel cells, but also in carbon capture and storage. This paper reviews the recent progress on the activation of biochar and its diverse present and future applications.

Activated carbons (ACs) have been used as electrode materials of electric double-layer capacitors (EDLC) due to their high specific surface areas (SSA), stability, and ecological advantages. In order to make high-energy-density ACs for EDLC, petroleum pitch (PP) precarbonized at 500–1000°C in N2 gas for 1 h was used as the electrode material of the EDLC after KOH activation. As the pre-carbonization temperature increased, the SSA, pore volume and gravimetric capacitance tended to decrease, but the crystallinity and electrode density tended to increase, showing a maximum volumetric capacitance at a medium carbonization temperature. Therefore, it was possible to control the crystalline structure, SSA, and pore structure of AC by changing the pre-carbonization temperature. Because the electrode density increased with increasing of the pre-carbonization temperature, the highest volumetric capacitance of 28.4 F/cc was obtained from the PP pre-carbonized at 700°C, exhibiting a value over 150% of that of a commercial AC (MSP-20) for EDLC. Electrochemical activation was observed from the electrodes of PP as they were pre-carbonized at high temperatures above 700°C and then activated by KOH. This process was found to have a significant effect on the specific capacitance and it was demonstrated that the higher charging voltage of EDLC was, the greater the electrochemical activation effect was.