This study was carried out to investigate the effect of grain size on the damping capacity of the Fe-26Mn-4Co-2Al damping alloy. α’ and ε-martensite were formed by cold working, and these martensites were formed with a specific direction and surface relief. With an increase in grain size, the volume fraction of α’ and ε-martensite increased by decrement the austenite phase stability. This volume fraction more rapidly increased in cold-rolled specimen than in the specimen that was not cold-rolled. The damping capacity also increased more with the augmentation an increased grain size and more rapidly increased in cold-rolled specimen than in the specimen that was not cold rolled. The effect of grain size on the damping capacity was larger in the cold-rolled specimen than the specimen that was not cold-rolled. Damping capacity linearly increased with an increase in volume fraction of ε-martensite. Thus, the damping capacity was affected by the ε-martensite.

This study was carried out to investigate the effect of deformation induced martensite on the damping capacity of Fe-26Mn-4Co-2Al damping alloy. α‘ and ε-martensite were formed by cold working, and; deformation induced martensite was formed with according to the specific direction and the surface relief. With an increasing degree of cold rolling, the volume fraction of α‘-martensite increased rapidly, while the volume fraction of ε-martensite decreased after rising to a maximum value at a specific level of cold rolling. Damping capacity was increased, and then decreased with an increasing of the degree of cold rolling. Damping capacity was influenced greatly by the volume fraction of ε-martensite formed by cold working, but the effect of the volume fraction of α‘-martensite have a actually on effect on the damping capacity.

Nanopowders of and FeAl were fabricated by high energy ball milling. Dense 4.25 composite was simultaneously synthesized and consolidated by high frequency induction heated combustion method within 2 min from mechanically activated powders. Consolidation was accomplished under the combined effects of a induced current and mechanical pressure of 80 MPa.

We report on the formation and chemical leaching of non-equilibrium alloy produced by rod milling. X-ray diffractometry, transmission electron microscopy, differential scanning calorimetry, scanning electron microscopy, and vibrating sample magnetometry were used to characterize the as-milled and leached specimens. After 400 h, only the peak of the body-centered cubic type was present in the XRD pattern. The entire rod milling process could be divided into three different stages of milling: agglomeration, disintegration, and homogenization. The saturation magnetization, decreased with increased milling time, the of the powders before milling was about 113.8 emu/g, the after milling for 400 h was about 11.55 emu/g. Leaching of the Al in KOH of the Al at room temperature from the as-milled powders did not induce any significant change in the diffraction pattern. After the leached specimen had been annealed at for 1 hour, the nanoscale crystalline phases were transformed into the bcc Fe, cubic Co, and phases. On cooling the specimen from 85, the degree of magnetization increased slightly, then increased sharply at approximately 364.8, indicating that the bcc phase had been transformed to the Fe and Co phases.

(NdㆍDy)-(FeㆍCoㆍAIㆍM)-B 합금에 Sn,Mo등을 첨가하여 그에 따른 미세구조와 열적안정성 및 자기적 특성 변화를 조사하였다. Sn과 Mo의 첨가는 (NdㆍDy)-(FeㆍCoㆍAIㆍM)-B 합금리본의 큐리온도를 크게 향상시켰으며 자기특성, 특히 보자력을 1KOe이상 증가시켰다. 그리고 이러한 현저한 보자력 증가는 입계형 defect인 disturbed grain boundary defect에 기인하는 것이라 판단되었다. 또한 Sn과 Mo 첨가원소는 irreversible loss를 각각 4%와 6% 감소시켜 리본자석의 열적안정성을 향상시켰다. 이는 Sn과 Mo의 첨가가 보자력을 크게 증가시켰기 때문이다. 한편 (NdㆍDy)-(FeㆍCoㆍAIㆍM)-B 리본자석들의 열저항온도(heat resistance temperature)는 irreversible loss와 직선관계를 이루었다.