Anodic aluminum oxide (AAO) has been widely used for the development and fabrication of nano-powder with various morphologies such as particle, wire, rod, and tube. So far, many researchers have reported about shape control and fabrication of AAO films. However, they have reported on the shape control with different diameter and length of anodic aluminum oxide mainly. We present a combined mild-hard (or hard-mild) anodization to prepare shape-controlled AAO films. Two main parameters which are combination mild-hard (or hard-mild) anodization and run-time of voltage control are applied in this work. The voltages of mild and hard anodization are respectively 40 and 80 V. Anodization was conducted on the aluminum sheet in 0.3 mole oxalic acid at 4oC. AAO films with morphologies of varying interpore distance, branch-shaped pore, diameter-modulated pore and long funnel-shaped pore were fabricated. Those shapes will be able to apply to fabricate novel nano-materials with potential application which is especially a support to prevent volume expansion of inserted active materials, such as metal silicon or tin powder, in lithium ion battery. The silicon powder electrode using an AAO as a support shows outstanding cycle performance as 1003 mAh/g up to 200 cycles.

투명 전도성 산화물로서 알루미늄과 붕소가 함께 도핑된 아연산화물(AZOB)이 900℃에서 분무 열분해법에 의해 제조되었다. 얻어진 마이크론 크기의 AZOB 분말은 알루미늄, 붕소 및 아연의 수용액으로부터 얻어진다. 분무 열분해로 얻어진 마이크론 크기의 AZOB 분말은 700℃에서 두 시간동안의 후 소성 과정과 24 시간 동안의 볼 밀링을 통해 나노 크기의 AZOB으로 변환된다. AZOB을 구성하는 일차 입자의 크기를 Debye-Scherrer 식에 의해 계산하였고 압축된 AZOB 펠렛의 표면 저항을 측정하였다.

The feasibility of obtaining highly dispersed aluminum oxide powders by the electrical explosion of aluminum conductors in an inert gas atmosphere and the subsequent oxidation of aluminum particles by water prior to their contact with air is demonstrated. For a specific surface area of the initial aluminum powder of 6.5/g, the corresponding specific surface area of the resultant aluminum oxide nanopowder was as large as 300/g.