Copper, mainly used as a material for outer canister, generates various corrosion products under aerobic and anaerobic conditions in the operational and/or post-closure phases of the deep geological repository. These products could affect performance of engineering barrier system (EBS) through interaction with surrounding bentonite that makes up the buffer and backfill materials. Accordingly, in this study, we suggested research items to be conducted to minimize degradation of EBS due to copper corrosion products, based on the phenomenological review results for copper corrosion mechanisms and interaction between resultant product and bentonite in the deep geological disposal environment. During the post-closure phase, condition in the disposal facility changes form aerobic to anaerobic over time, and thereby, causes and products of copper corrosion vary. Under aerobic condition, copper corrosion is mainly induced by oxygen (O2) in the repository, chloride (Cl-) and carbonate (CO3 2-) ions from groundwater flowing into the facility, resulting in corrosion products such as cuprite (Cu2O), tenorite (CuO), atacamite (CuCl2·3Cu(OH)2) and malachite (Cu2CO3(OH)2). And, copper corrosion under anaerobic condition is primarily due to hydrogen sulfide (H2S) and sulfate (SO4 2-) in groundwater flowing into the facility, leading to formation of chalcocite (Cu2S) and covellite (CuS) as corrosion products. Depending on environment of the disposal facility, copper corrosion products are dissolved and ionized to Cu2+ in groundwater, and subsequently adsorbed on the nearby smectite. Then, it causes a cation exchange reaction with exchangeable cations in the interlayer of smectite. As a result of reviewing the previous experiments, it was confirmed that Cu2+-exchanged bentonite has a slightly reduced basal spacing and swelling capacity. From the results as above, there is a possibility that performance of EBS may be degraded due to copper corrosion products. To minimize its effect of degradation in the domestic facility, items to be further studied are as follows: (a) Method for reducing copper corrosion such as selection of appropriate material and structure for the canister, and (b) How to control dissolution of copper canister product into groundwater through predicting type and ionization process. The results of this study could be directly used to developing design concept of EBS for the domestic disposal facility and to establishing roadmap of future R&D programs.

Bentonite is a widely used buffer material in high-level radioactive waste repositories due to its favorable properties, including its ability to swell and low permeability. Bentonite buffers play an important role in safe disposal by providing a low permeability barrier and preventing radionuclides migration into the surrounding rock. However, the long-term performance of the bentonite buffer is still an area of research, and one of the main concerns is the erosion of the buffer due to swelling and groundwater flow. Erosion of the bentonite buffer can have a significant impact on repository safety by reducing the integrity of the buffer and forming colloids that can transport radionuclides through groundwater, potentially increasing the risk of radionuclide migration. Therefore, understanding the mechanisms and factors that influence the erosion of the bentonite buffer is critical to the safety assessment of high-level radioactive waste repositories. In this study, we attempted to develop the bentonite buffer erosion model using Adaptive Processbased total system performance assessment framework for a geological disposal system (APro) proposed by the Korea Atomic Energy Research Institute (KAERI). First, the erosion phenomenon was divided into two stages: bentonite buffer penetration into rock fractures and colloid formation. As an initial step in the development of the buffer erosion model, a bentonite buffer intrusion into the fracture and consequent degradation of buffer property were considered. For this purpose, a tworegion model based on the dynamic bentonite diffusion model was adopted which is one of the methods for simulating bentonite buffer intrusion. And, it was assumed that the buffer properties, such as density, porosity and permeability, thermal conductivity, modulus of elasticity, and mechanical strength, are degraded as the buffer erodes. The bentonite buffer degradation model developed in this study will serve as a foundation for the comprehensive buffer erosion model, in conjunction with the colloidal formation model in the future.