Biomass adsorbents were prepared from fallen oak leaves. In the activation process for fallen oak leaves, various operating parameters such as the activation temperature (600-900°C), steam injection rate (5-15 cc/hr), and steam injection time (1- 3 hr) were adopted. For analyses of the manufactured adsorbent, various methods such as scanning electron microscope (SEM), measurements of the BET surface area and chemical composition analyses were adopted. Regarding major adsorption characteristics, the adsorption equilibrium capacity was measured using batch type experimental apparatus for various biomass adsorbents. The experimental result showed that the H2S adsorption equilibrium capacity of the adsorbent made from fallen oak leaves decreased as the activation temperature and steam injection rate increased for a given range.

산업의 발전과 경제규모의 팽창에 따라 에너지소비가 크게 증가되는 가운데 대기오염물질배출이 크게 늘어나면서 심각한 환경문제를 야기하고 있다. 이중에서 황화수소(H2S)는 계란 썩는 냄새가 나는 무색의 유독한 기체로서 인체의 위장이나 폐에 흡수되어 질식, 폐 질환, 신경중추마비 등을 발생시키고 있다. H2S 가스는 폐기물 매립장, 석유 정제업, 펄프공업, 도시가스 제조업, 암모니아공업, 하수처리장 등 다양한 곳에서 발생하고 있으며, 이를 처리하기 위하여 심냉법, 흡수법, 막분리법, 흡착법 등 여러 가지 처리방법이 제시되었다. 본 연구에서는 실험실규모의 장치를 이용하여 바이오매스 부산물을 활용한 악취저감용 흡착소재개발을 위해 밤껍질을 대상으로 탄화, 스팀활성처리등의 과정을 거쳐 흡착제를 제조하였으며, BET분석, SEM등을 이용한 물성분석, 회분식의 흡착평형실험, 악취 모니터링실험을 통한 흡착특성을 고찰하였다. 실험결과, 밤껍질을 활용하여 탄화 및 활성처리과정을 거치면서 얻을 수 있는 흡착제의 수율은 15∼20%에 해당되는 것으로 밝혀졌다. 또한, 밤껍질부산물은 스팀을 이용한 활성처리 과정에서 온도가 증가할수록. 시간이 증가할수록 스팀-탄소 화학반응에 의해 내부기공이 커지면서 비표면적이 증가되는 것으로 밝혀졌다. 아울러, 밤껍질부산물을 소재로한 흡착제의 황화수소 평형흡착능과 파과성능은 활성탄대비 비교적 우수한 성능을 보임으로써, 악취제거용 흡착소재로 활용성이 클 것으로 예상되었다.