In order to prepare anode materials for high power lithium ion secondary batteries, carbon composites were fabricated with a mixture of petroleum pitch and coke (PC) and a mixture of petroleum pitch, coke, and natural graphite (PCNG). Although natural graphite has a good reversible capacity, it has disadvantages of a sharp decrease in capacity during high rate charging and potential plateaus. This may cause difficulties in perceiving the capacity variations as a function of electrical potential. The coke anodes have advantages without potential plateaus and a high rate capability, but they have a low reversible capacity. With PC anode composites, the petroleum pitch/cokes mixture at 1:4 with heat treatment at 1000 oC (PC14-1000C) showed relatively high electrochemical properties. With PC-NG anode composites, the proper graphite contents were determined at 10~30 wt.%. The composites with a given content of natural graphite and remaining content of various petroleum pitch/cokes mixtures at 1:4~4:1 mass ratios were heated at 800~1200 oC. By increasing the content of petroleum pitch, reversible capacity increased, but a high rate capability decreased. For a given composition of carbonaceous composite, the discharge rate capability improved but the reversible capacity decreased with an increase in heat treatment temperature. The carbonaceous composites fabricated with a mixture of 30 wt.% natural graphite and 70 wt.% petroleum pitch/cokes mixture at 1:4 mass ratio and heat treated at 1000 oC showed relatively high electrochemical properties, of which the reversible capacity, initial efficiency, discharge rate capability (retention of discharge capacity in 10 C/0.2 C), and charge capacity at 5 C were 330 mAh/g, 79 %, 80 %, and 60 mAh/g, respectively.

High crystallinity coke-based activated carbon (hc-AC) is prepared using a potassium hydroxide solution to adsorb carbon dioxide (CO2). The CO2 adsorption characteristics of the prepared hc-AC are investigated at different temperatures. The X-ray diffraction patterns indicate that pitch-based cokes prepared under high temperature and pressure have a high crystal structure. The textural properties of hc-AC indicate that it consists mainly of slit-like pores. Compared to other textural forms of AC that have higher pore volumes, this slit-poreshaped hc-AC exhibits higher CO2 adsorption due to the similar shape between its pores and CO2 molecules. Additionally, in these high-crystallinity cokes, the main factor affecting CO2 adsorption at lower temperature is the pore structure, whereas the presence of oxygen functional groups on the surface has a greater impact on CO2 adsorption at higher temperature.

Petroleum pitch and coke with wet mixture method or with dry mixture method were investigated to develop the composite anodic carbon material of high power lithium ion battery. Cokes coated with pitch were obtained by the heat treatment of mixture of cokes and pitch with different weight ratios at 800~1200℃. The charge and discharge characteristic of the consequent composite anodic carbon material assembled in batteries was tested. Cokes with wet mixture method have a smooth surface and their capacity changed little with changing temperature and content as compared to the cokes with dry mixture method. Although the reversible capacities showed different values by the anode manufacturing method, the composite anode with the mixture of 20 wt% of petroleum pitch and 80 wt% of coke showed the higher power capability and initial efficiency than the pitch based anode. However, the reversible capacity of the composite anode showed the reduced value as compared with the pitch based anode.

석탄과 철광석은 산업발달의 시작부터 현재까지 지속적으로 사용되고 있다. 이에 따라 수반된 석탄 및 철광석 정제산업의 발달은 석탄철광폐수의 양적 증가를 초래하여 그 처리가 많은 관심 속에 활발하게 연구되고 있다. 석탄철광폐수는 페놀, 시안과 같은 독성 물질 뿐 만 아니라 혐기성미생물과 경쟁관계에 있는 황산염환원균활성증가를 초래하는 SO42-를 고농도로 함유한다. 이 석탄철광폐수의 처리법으로는 물리적, 화학적, 생물학적 처리가 다양하게 연구되어왔는데, 고농도의 폐수처리에 익히 알려진 혐기성미생물을 이용한 석탄철광폐수의 처리는 경제성과 재생에너지 측면에서 최근 큰 관심을 받고 있다. 하지만 폐수에 함유된 페놀, 시안, 등과 같은 독성물질이 생물학적 처리에 심각한 저해를 초래할 수 있어 문제로 지적되고 있으나 그 독성에 대한 현재까지의 연구는 미진한 형편이다. 이에 본 연구는 입상 혐기성미생물이 석탄철광폐수 소화 시 받게 되는 급성독성에 대하여 실험적 고찰을 진행하고 그 적응 방안을 연구하였다. 석탄철광폐수는 석탄철광정제의 완료시점에 실폐수 샘플을 채취하여 사용하였다. 폐수특성 분석결과 pH 7, 페놀 589±23 mg/L, 시안 49 mg/L, 암모니아성질소 39±9 mg/L, SO4-2는 735 mg/L이며 화학적 산소요구량은 3.9 g/L으로 나타났다. 석탄철광폐수에 대한 물벼룩 급성독성시험 결과 TU가 28로 매우 높게 측정되었다. 이 폐수에 UASB의 입상슬러지를 이용하여 혐기성소화를 수행하였다. 약 20일간 유기물 부하 0.6 g COD/L/day에서 초기 적응을 수행하였고, 혐기성소화조의 정상상태에서 COD 제거율은 98%, 메탄수율은 약 80 mL CH4/g COD로 나타났다. 이 혐기성소화조가 석탄철광폐수 유기물부하 0.76 g COD/L/day에 노출 되었을 경우 미생물의 활성을 모니터링한 결과, 폐수유입 즉시 메탄가스발생이 80% 이상 감소되는 강한 독성이 감지되었으며 COD 제거효율은 점차 감소하여 약 20일 후 10%로 낮아졌다. 유출수 내 페놀은 약 210 mg/L로 제거율 60%을 나타났지만 시안은 106 mg/L로 분해되지 않고 축적되어 유입 대비 2배가량 증가하였다. SO4-2 는 2000 mg/L로 급격하게 농도가 증가한 후 약 20일 후 1000 mg/L 이하로 감소하였다. 이로보아 석탄철광폐수 내 시안과 황화합물로 인하여 혐기성미생물 내의 메탄균의 저해가 이루어짐을 짐작할 수 있다. VFA 분석결과는 산발효균과 메탄발효균의 공생관계가 파괴되었음을 보여주었다. 더불어 높은 SO4-2 농도는 황산염환원균과의 경쟁이 유도될 수 있는 농도로 밝혀졌다. 이러한 석탄철광폐수의 급성독성은 고농도의 독성물질 제거를 위한 전처리 혹은 혐기성미생물의 적응기간이 필요함을 나타내었으며, 후자를 선택하여 약 30일 간 단계적인 미생물의 독성적응절차를 거친 결과 급성독성을 극복하고 유기물 및 페놀 분해가 점진적으로 가능함을 확인 하였다.