Composite adsorbents were prepared by mixing water plant sludge with phenolic resin having the ratio of 1 : 1, 1 : 2, and 1 : 3 respectively, curing from 100℃ to 170℃ under N2 atmosphere, and then activating with N2 at 700℃. Thermal property, specific surface area and morphology of the composite adsorbents as well as their precursors were measured by TGA, BET and SEM respectively. Removal efficiency of the composite adsorbents to NH4+ and TOC was compared with those of commercial zeolite and activated carbon. The adsorbents presented very promising TOC removal efficiency of 98%, which was identical level to that of commercial activated carbon while they displayed removal efficiency, only 32%, of NH4+. Therefore, this composite adsorbent considered as the alternative material of commercial activated carbon, used as an expensive removal agent of organic substances and THM in water treatment plant and it also suggested a possibility of practical application in other processes.

아미드옥심기와 복합재료 섬유흡착제를 제조하였고 해수로부터 우라늄이온의 분리 특성을 조사하였다. 흡착량은 흡착시간이 증가함에 따라 증가하였고 An:TEGMA:DVB의 몰비가 1:0.1:0.003인 수지가 pH 8 부근에서 최대 흡착능을 나타내었다. 또한 흡착량은 CFA에 첨가한 흡착제의 양이 증가함에 따라 증가하였으며 1시간 까지 선형적으로 증가하였고, 25˚C에서 최대흡착량을 나타내었다. 한편 Ca, Mg 이온은 흡-탈착 cycle이 반복될수록 증가하였으며 그양은 각각 0.3, 0.9mmole/g-Ads로 우라늄 이온의 그것보다 매우 낮았다. 흡착된 우라늄 이온의 탈착은 흡착제의 종류에 관계없이 약 30분 이내에 거의 100% 탈착되었다.

해수로 부터 우라늄 분리를 위한 아미드옥심형 섬유복합재료 흡착제를 제조하였고, IR, 팽윤도 실험, CHN 원소분석, SEM 및 흡착능 실험을 통하여 그 특성을 알아보았다. AN-TEGMA 및 AN-TEGMA-DVB 공중합체의 팽윤율과 수율은 가교제의 함량이 증가할 수록 감소하였으며, 수율은 AN-TEGMA 공중합체의 경우 85-92%였고 AN-TEGMA-DVB 공중합체는 82-88%였다. 다공도도가교체의 함량이 증가할 수록 감소하였으며 AN-TEGMA-DVB 공중합체가 AN-TEGMA 공중합체보다 작았다. 또한 전자현미경 관찰 결과 제조한 섬유 복합재료 흡착제의 표면에 흡착제가 고루 분포되어 있는 것을 확인하였고, 흡착제의 최적 첨가량은 40wt%이었다. 섬유복합재료 흡착제의 우라늄 흡착량은 pH 8 부근에서 최대 였으며, 해수의 pH가 8.3임을 감안할 때 해수 우라늄 분리에 적합한 소재 임을 알 수 있었다.