Radioactive waste generated during decommissioning of nuclear power plants is classified according to the degree of radioactivity, of which concrete and soil are reclassified, some are discharged, and the rest is recycled. However, the management cost of large amounts of concrete and soil accounts for about 40% of the total waste management cost. In this study, a material that absorbs methyl iodine, a radioactive gas generated from nuclear power plants, was developed by materializing these concrete and soil, and performance evaluation was conducted. A ceramic filter was manufactured by forming and sintering mixed materials using waste concrete, waste soil, and by-products generated in steel mills, and TEDA was attached to the ceramic filter by 5wt% to 20wt% before adsorption performance test. During the deposition process, TEDA was vaporized at 95°C and attached to a ceramic filter, and the amount of TEDA deposition was analyzed using ICP-MS. The adsorption performance test device set experimental conditions based on ASTM-D3808. High purity nitrogen gas, nitrogen gas and methyl iodine mixed gas were used, the supply amount of methyl iodine was 1.75 ppm, the flow rate of gas was 12 m/min, and the supply of water was determined using the vapor pressure value of 30°C and the ideal gas equation to maintain 95%. Gas from the gas collector was sampled to analyze the removal efficiency of methyl iodine, and the amount of methyl iodine detected was measured using a methyl iodine detection tube.

우라늄 토양 및 콘크리트 폐기물의 동전기 제염 후 방사성폐기물의 시멘트 고화특성을 분석하기 위하여, 시멘트 고화 유동성 시험을 수행하고 시멘트 고화 시료를 제작하였다. 시멘트 고화시료에 대하여 압축강도, pH, 전기전도도, 방사선조사 효과 및 부피증가를 분석하였다. 방사성폐기물의 시멘트 고화의 작업 적정도는 175~190% 정도였다. 시멘트 고화시료의 방사선 조사 후 압축강도는 방사선 조사 전 압축강도 보다 약 15% 감소하였으나, 한국원자력환경공단 인수기준 (34 kgf·cm-2)을 만족하였다. 동전기 제염 후 방사성폐기물의 시멘트 고화 시료에 대한 SEM-EDS 분석결과, 알루미늄상은 시멘트와 잘 결합 한 형상을 나타낸 반면, 칼슘상은 시멘트와 분리된 형상을 나타내었다. 방사성폐기물의 시멘트 고화 부피는 시멘트에 대한 폐기물의 배합과 수분량에 따라 다르게 나타났다. 방사성폐기물의 시멘트 고화 부피(C-2.0-60)는 약 30% 증가였으며 동전기 제염 후 생성된 방사성폐기물의 영구처분은 적절하다고 판단되었다.