In this study, STS 316L powders with 3 wt.% Cu and 1 wt.% Sn known as corrosion-resistance reinforce- ment elements, are prepared to make different kinds of specimens, in which, 3 wt.% Cu and 1 wt.% Sn are added in different forms by mixing, alloying and fully alloying. After sintering in the same condition, the corrosion resistance, wear resistance and their mechanical properties of specimens are tested respectively. According to the comparison, STS 316L specimen sintered at 1270o C showed the most excellent mechanical property: HRB 78 (hardness), 1130.7 MPa (RCS), 26.6% (Fraction Wear), It was similar with the specimen made of STS316L and fully alloyed Cu and Sn pow- ders, meanwhile, the latter one appears the best corrosion resistance, 75hrs-salt immersion test results. In addition, the specimens with Cu and Sn powders additive showed relatively worse wear resistance in compared with STS316L spec- imen.

강구조물의 고력볼트 마찰접합부에 있어서 마찰면의 부식은 장기적으로 마찰력 감소와 접합부 내력저하를 초래한다. 본 연구는 고력볼트 접합부의 부식을 방지하고 소요 역학적 성질을 만족시키기 위해 접합부의 마찰면에 Zn/Al 금속용사 방청처리 한 고력볼트 접합부를 대상으로 마찰면의 표면처리방법과 피막두께를 주요 변수로 하여 인장시험을 실시하였고, 실험으로 부터 마찰면 표면거칠기와 미끄럼계수를 측정하였다. 무도장 샌드블라스트 처리한 접합부 및 샌드블라스트 처리 후 금속용사를 실시한 볼트 접합부의 미끄럼 계수는 국내 규준의 규정 값과 비교하여 동등 이상의 우수한 미끄럼계수 값을 나타냈다.