Pollution of chloride ion-reinforced concrete can trigger active corrosion processes that reduce the useful life of structures. Multifunctional materials used as a counter-electrode by electrochemical techniques have been used to rehabilitate contaminated concrete. Cement-based pastes added to carbonaceous material, fibers or dust, have been used as an anode in the non-destructive Electrochemical Chloride Extraction (ECE) technique. We studied the performance of the addition of Carbon Fiber (CF) in a cement-graphite powder base paste used as an anode in ECE of concretes contaminated with chlorides from the preparation of the mixture. The experimental parameters were: 2.3% of free chlorides, 21 days of ECE application, a Carbon Fiber Volume Fraction (CFVF) of 0.1, 0.3, 0.6, 0.9%, a lithium borate alkaline electrolyte, a current density of 4.0 A / m2 and a cement/graphite ratio of 1.0 for the paste. The efficiency of the ECE in the traditional technique using metal mesh as an anode was 77.6% and for CFVF of 0.9% it was 90.4%, with a tendency to increase to higher percentages of the CFVF in the conductive cement-graphite paste, keeping the pH stable and achieving a homogeneous ECE in the mass of the concrete contaminated with chlorides.

Carbonaceous thin films were prepared from acetylene and argon gases by plasma assisted chemical vapor deposition (Plasma CVD) at 873 K. The carbonaceous thin films were characterized by mainly Raman spectroscopy, and their electrochemical properties were studied by cyclic voltammetry and charge-discharge measurements in propylene carbonate (PC) solution. Raman spectra showed that crystallinity of carbonaceous thin films is correlated by the applied RF power. The difference of the applied RF power also affected on the results of cyclic voltammetry and charge-discharge measurements. In PC solution, intercalation and de-intercalation of lithium ion can occur as well as in the mixed solution of EC and DEC.