Cu matrix composites reinforced with chopped carbon fiber (CF), which is cost effective and can be well dispersed, are fabricated using electroless plating and hot pressing, and the effects of content and alignment of CF on the thermal properties of CF/Cu composites are studied. Thermal conductivity of CF/Cu composite increases with CF content in the in-plane direction, but it decreases above 10% CF; this is due to reduction of thermal diffusivity related with phonon scattering by agglomeration of CF. The coefficient of thermal expansion decreases in the in-plane direction and increases in the through-plane direction as the CF content increases. This is because the coefficient of thermal expansion of the long axis of CF is smaller than that of the Cu matrix, and the coefficient of thermal expansion of its short axis is larger than that of the Cu matrix. The thermal conductivity is greatly influenced by the agglomeration of CF in the CF/Cu composite, whereas the coefficient of thermal expansion is more influenced by the alignment of CF than the aggregation of CF.

강섬유 보강 자기충전 콘크리트(Steel Fiber Reinforced Self-Compacting Concrete, SFRSCC)는 사회기반 시설이나 초고층 빌딩, 원자력 발전 시설, 병원, 댐, 수로 등 전반적으로 널리 사용되어지고 있는 재료이다. SFRSCC는 짧고, 개별적인 보강 섬유로 인해 일반적인 자기충전 콘크리트(Self-Compacting Concrete, SCC) 보다 인장 강도, 연성, 휨 강성 등에서 뛰어난 성능을 보인다. 하지만 SFRSCC의 이러한 성능은 섬유의 방향성에 의해 크게 좌우되는 경향이 있다. 짧고 개별적인 섬유들은 타설 과정에서 섬유의 방향성을 컨트롤 할 수 없기 때문에 무분별하게 콘크리트 내에 위치하게 된다. 섬유의 방향이 제어되지 않은 상태에서 콘크리트의 경화가 진행될 경우 휨 강성과 인장 강도의 저하를 야기하고, 이는 예상 강도 미달의 원인이 될 수 있기 때문에 SFRSCC를 사용할 때 섬유의 정렬은 중요한 요소가 된다. 따라서 본 연구에서는 유한 요소법을 사용하여 타설 공정 중 콘크리트 매트리스의 점도 및 입구 속도가 섬유 방향에 미치는 영향에 대해 분석하였다.