The optical fibers tend to have poor machinability because of its hardness and brittleness. In the previous study, we applied the electrochemical discharge machining to fabricate the tip of the optical fiber. We could machine the optical fiber using the electrochemical discharge machining however the machined optical fiber tip had rough surface. In this study, we use electrochemical discharge machining with rotation tool which of the rough-grinding and finishing-grinding process to obtain a smooth surface of the side firing fiber. As a result, we are able to machine the optical fiber tip with smooth surface effectively from the proposed fiber machining process and the emission from the side-firing fiber clearly demonstrated the directional emission as the emission beam was reflected at 80 ° relative to the fiber axis.

뇌록은 조선시대 건축물의 바탕칠(가칠)에 사용된 녹색 안료이며, 불국사 대웅전 등 주요 건축물의 단청에 사용되었다. 본 연구에서는 한국 전통 안료 원료인 뇌록을 이용하여 소성온도에 따른 광물학적 특성 변화를 살펴보았다. 포항 뇌성산 일대에 국부적으로 산출하고 있는 뇌록은 주구성 광물이 셀라도나이트(celadonite)이며, 주요 구성 원소는 Fe, Si, K, Mg 등으로 주로 Fe가 풍부한 운모류임을 알 수 있다. 105℃~1000℃까지 단계적 소성실험 결과, 색상이 녹색 → 담녹색 → 갈색 → 적색으로 변하였으며, 열분석에서는 616℃ 부근에서 결정수의 탈수작용에 의한 흡열반응이 확인되었다. 광물의 변화는 600℃ 이상에서 결정면[(11-1), (02-1)]이 붕괴되고, 1000℃ 이상에서 철산화물이 형성되었다. 따라서 뇌록의 정출 온도가 600℃ 이하인 것으로 추정되며, 셀라도나이트만이 확인되는 것으로보아 Stage I 단계만의 변질을 겪은 것으로 판단된다.