Li1.3Al0.3Ti1.7(PO4)3(LATP) is considered a promising material for all-solid-state lithium batteries owing to its high moisture stability, wide potential window (~6 V), and relatively high ion conductivity (10-3–10-4 S/cm). Solid electrolytes based on LATP are manufactured via sintering, using LATP powder as the starting material. The properties of the starting materials depend on the synthesis conditions, which affect the microstructure and ionic conductivity of the solid electrolytes. In this study, we synthesize the LATP powder using sol-gel and co-precipitation methods and characterize the physical properties of powder, such as size, shape, and crystallinity. In addition, we have prepared a disc-shaped LATP solid electrolyte using LATP powder as the starting material. In addition, X-ray diffraction, scanning electron microscopy, and electrochemical impedance spectroscopic measurements are conducted to analyze the grain size, microstructures, and ion conduction properties. These results indicate that the synthesis conditions of the powder are a crucial factor in creating microstructures and affecting the conduction properties of lithium ions in solid electrolytes.

Impedancemetric NOx (NO and NO2) gas sensors were designed with a stacked-layer structure and fabricated using LaCrxCo1-xO3 (x = 0, 0.2, 0.5, 0.8 and 1) as the receptor material and Li1.3Al0.3Ti1.7(PO4)3 plates as the solid-electrolyte transducer material. The LaCrxCo1-xO3 layers were prepared with a polymeric precursor method that used ethylene glycol as the solvent, acetyl acetone as the chelating agent, and polyvinylpyrrolidone as the polymer additive. The effects of the Co concentration on the structural, morphological, and NOx sensing properties of the LaCrxCo1-xO3 powders were investigated with powder Xray diffraction, field emission scanning electron microscopy, and its response to 20~250 ppm of NOx at 400 oC (for 1 kHz and 0.5 V), respectively. When the as-prepared precursors were calcined at 700 oC, only a single phase was detected, which corresponded to a perovskite-type structure. The XRD results showed that as the Co concentration of the LaCrxCo1-xO3 powders increased, the crystal structure was transformed from an orthorhombic phase to a rhombohedral phase. Moreover, the LaCrxCo1-xO3 powders with 0 ≤ x < 0.8 had a rhombohedral symmetry. The size of the particles in the LaCrxCo1-xO3 powders increased from 0.1 to 0.5 μm as the Co concentration increased. The sensing performance of the stack-structured LaCrxCo1-xO3/Li1.3Al0.3Ti1.7(PO4)3 sensors was found to divide the impedance component between the resistance and capacitance. The response of these sensors to NO gas was more sensitive than that to NO2 gas. Compared to other impedancemetric sensors, the LaCr0.8Co0.2O3/Li1.3Al0.3Ti1.7(PO4)3 sensor exhibited good reversibility and reliable sensingresponse properties for NOx gases.