Large-size graphene samples are successfully prepared by combining ultrosonic assisted liquid phase exfoliation process with oxidation-deoxidation method. Different from previous works, we used an ultrasound-treated expanded graphite as the raw material and prepared the graphene via a facile oxidation-reduction reaction. Results of X-ray diffraction and Raman spectroscopy confirm the crystal structure of the as-prepared graphene. Scanning electron microscopy images show that this kind of graphene has a large size (with a diameter over 100 μm), larger than the graphene from graphite powder and flake graphite prepared through single oxidation-deoxidation method. Transmission electron microscopy results also reveal the thin layers of the prepared graphene (number of layers ≤3). Furthermore, the importance of preprocessing the raw materials is also proven. Therefore, this method is an attractive way for preparing graphene with large size.

결정성 탄소물질은 결합의 형태에 따라 carbyne (sp1, 1D 구조), graphite (sp2+π, 2D), diamond (sp3, 3D) 구조 로 나뉜다. 특히 sp2 결합에 기반한 나노물질은 fullerene (0D), 탄소나노튜브 (1D or quasi-2D), 그래핀 (2D) 으로 나뉜 다. 탄소나노튜브와 그래핀은 물리적으로 여러 가지 뛰어난 특성이 있어 구조재나 광전자 재료, 멤브레인 등 다양한 분 야에 응용가치가 높다. 하지만 이들 나노재료는 강하게 응집되는 성질이 있어 용액에 분산할 필요가 있다. 특히 이는 용 액 상에서 박리, 안정화의 과정을 거쳐야 안정적으로 분산된 상태를 유지할 수 있다. 본 고에서는 탄노나노튜브나 그래 핀이 용매에서 박리되어