Chlor-alkali (CA) membranes as key materials to generate chlorine gas and sodium hydroxide are composed of sulfonic acid layer (S-layer) and carboxylic acid layer (C-layer) to provide fast sodium ion transport and slow hydroxide ion diffusion, respectively. Aciplex F, a representative CA membrane is made in a double layer form via thermal adhesion of both layers after each single layer film is independently fabricated. Unfortunately, the membrane fabrication induces delamination particularly in their interface as a result of hydroxide ion diffusion occurring during CA operation, leading to rapid increase in electrochemical overpotential. In this study, selective chemical conversion technique was developed to solve the delamination issue. Their effectiveness was proved by applying the same concept to a wide range of PFSA membrane.

동해 영덕 연안의 저염수를 보기 위하여 지난 2010년 격월별(2월 23일, 4월 6일, 6월 8일, 8월 19일, 10월 6일, 12월 20일)로 20개의 정점에서 CTD 관측을 수행하였다. 혼합층은 여름에 약 10 m 깊이로 얕았으며, 겨울에 약 20 m 깊이에서부터 저층까지 혼합층을 나타내었다. 연중 5℃ 이하의 찬 물이 수온 약층 이심을 점하고 있었다. 염분 약층은 8월에는 깊이 20 m에, 10월에는 깊이 40 m에 분포하였으며 연중 가장 뚜렷하였다. 뚜렷한 저염수는 10월에 깊이 10 m에서 나타났는데, 10월에 강수량-증발량의 값이 음을 보였다, 이것은 10월에 영덕 연안에서 나타나는 저염수가 이류되어 온 것임을 시사하였다. 동해의 영덕 연안에서 나타나는 저염수는 동한 난류가 주요한 역할을 하는 것으로 보여진다.