Impact damages induced by a low-velocity impact load on carbon fiber reinforced polymer (CFRP) composite plates fabricated with various stacking sequences were studied experimentally. The impact responses of the CFRP composite plates were significantly affected by the laminate stacking sequences. Three types of specimens, specifically quasi-isotropic, unidirectional, and cross-ply, were tested by a constant impact carrying the same impact energy level. An impact load of 3.44 kg, corresponding to 23.62 J, was applied to the center of each plate supported at the boundaries. The unidirectional composite plate showed the worst impact resistance and broke completely into two parts; this was followed by the quasi-isotropic lay-up plate that was perforated by the impact. The cross-ply composite plate exhibited the best resistance to the low-velocity impact load; in this case, the impactor bounced back. Impact parameters such as the peak impact force and absorbed energy were evaluated and compared for the impact resistant characterization of the composites made by different stacking sequences.
충격 하중 재하 실험의 경우 빠른 하중 재하 속도로 인해 실험 데이터를 측정하는 방법에 있어 많은 어려움이 있다. 또한 부재의 국부적 손상을 측정하지 못함으로써 부재의 동적 거동을 왜곡하는 문제점이 존재한다. 따라서, 본 연구에서는 충격 실험에서의 한계를 극복하기 위하여 명시적(explicit) 유한요소 해석 프로그램인 LS-DYNA를 이용하여 FRP Sheet 및 강섬유로 보강된 콘크리트의 저속 충격 하중 하에서의 동적 거동을 분석하였다. 해석 모델은 1방향 및 2방향 부재이며 충격 하중 재하 시 부재의 국부적 파괴를 고려하고 있다. 해석결과 강섬유에 의해 보강된 SFRC와 UHPC 부재의 경우 충격 저항성능이 크게 향상되었다. FRP Sheet로 보강한 경우 GFRP가 CFRP보다 우수한 충격 저항 성능을 보였으며 FRP Sheet의 방향성에 의한 영향은 크게 나타나지 않았다. 본 연구에서 수행된 해석은 충격 실험 결과와의 비교를 통해 그 신뢰성이 검증되었다.