Biaxially textured Ni tapes were fabricated by a cold working and recrystallization heat treatment processes from powder compact rods. The processing parameters associated with the cube texture formation in Ni tapes were systematically investigated by using X-ray diffraction and pole-figure analysis. The Ni powder used in this study was 5 m in size and 99.99% in purity. To find the optimum sintering temperature, tensile tests were performed for Ni rods sintered at various temperatures. The Ni rods sintered at 100 showed poor elongation and low fracture strength, while the Wi rods sintered above 100 revealed good mechanical properties. The higher elongation and fracture strength of the Ni rods sintered at higher temperatures than 100 are attributed to the full densification of the sintered rods. The sintered Ni rods were cold-rolled with 5% reduction to the final thickness of 100 m and then annealed for development of rube texture in rolled Ni tapes. The annealed Ni tapes depicted strong cube texture with FWHM(full-width at half-maximum) of in-plane and out-of-plane in the range of 8 to 10. The NiO deposited on the Ni tapes by MOCVD process showed good epitaxy with FWHM=10, which indicates that the Ni tapes can be used as a substrate for YBCO coated conductors.

MCFC 작동온도인 650˚C에서 음극의 creep과 소결에 의한 구조적 변형을 막기 위해 기계적 합금법에 의한 Ni-WC분말을 합금화하여 변형에 대한 저항성을 증대시키고자 하였다. 80시간동안 어트리션 밀링을 실시한 분말은 XRD 분석결과 결정규칙이 파괴된 비정질 상을 보였다. 제조된 분말은 적당한 점도의 슬러리로 제조후 테이프 캐스팅법에 의해 green sheet를 제조하였다. 제조된 박판의 두께는 0.9mm였고, 평균 기공 크기는 3~5μm, 기공율은 55%였다. 소결체의 XRD 분석결과 2차성은 생성되지 않았으며, SEM 및 dot-Mapping image를 통해 Ni matrix 안에 W 입자가 미세하고 균일하게 분포되어 있어 고용강화 및 분산강화를 통해 Ni 음극의 기계적 특성을 향상시킬 것으로 기대된다.