In this study, waste corrugated paper was used as carbon precursor with KOH-NaOH mixture (mole ratio was 51:49 and the melting point is 170 °C) as activator to prepare porous carbon at different reaction temperature and different mass ratio of KOH-NaOH mixture/waste corrugate paper fiber. The micro-morphology, pore structure information and composition of porous carbon were analyzed, and the formation mechanism of pores was investigated. The effect of activator amount and pyrolysis temperature on the morphology and structure of porous carbon were studied. The adsorption capacity of porous carbon was evaluated with the methylene blue as model pollutant. The effect of adsorbent amount, adsorption time and temperature on the adsorption performance of the porous carbon were analyzed. The maximum specific surface area is 1493.30 m2 ·g−1 and the maximum adsorption capacity of methylene blue is 518 mg·g−1. This study provides a new idea for efficient conversion and utilization of waste paper.

인쇄에서 종이의 인쇄적성은 인쇄품질을 결정하는 중요한 요소이며, 이를 보완하기 위해 많은 연 구들이 진행되어 왔다. 특히, 잉크젯에 의한 종이의 인쇄적성은 앞으로 전자융합산업의 발달을 고려해본 다면 더욱 주요한 연구가 될것이다. 따라서, 본 연구는 잉크젯 시스템에서 사용하는 CMYK 프로세스 잉 크의 인쇄적성을 파악하고 종이의 특성에 따라 색재현 정도를 ICC 프로파일값을 활용하여 분석하고자 하 였다. 잉크젯의 토출 특성을 이해하기 노즐에서의 잉크 유동을 시뮬레이션 하였고 종이의 재질이 다른 두 종(갱지 및 인화지)의 피인쇄체 위에 각기 다른 망점으로 인쇄하여 색재현 평가를 실시하였다. 각 종이의 관련 특징들 즉, 거칠음도, 투기도, 광택도 및 압축도,과 이에따른 색재현 특성을 ICC 프로파일모니터링에 쓰이는 ΔE값으로 표현하였다. 그 결과 상대적으로 종이의 낮은 거칠음도와 투기도 그리고 높은 압축력을 가지는 인화지에서 더 높은 색재현이 이루어짐을 알 수 있었다.