Pretreatment system of desalination process using seawater reverse osmosis(SWRO) membrane is the most critical step in order to prevent membrane fouling. One of the methods is coagulation-UF membrane process. Coagulation-UF membrane systems have been shown to be very efficient in removing turbidity and non-soluble and colloidal organics contained in the source water for SWRO pretreatment. Ferric salt coagulants are commonly applied in coagulation-UF process for pretreatment of SWRO process. But aluminum salts have not been applied in coagulation-UF pretreatment of SWRO process due to the SWRO membrane fouling by residual aluminum. This study was carried out to see the effect of residual matal salt on SWRO membrane followed by coagulation-UF pretreatment process. Experimental results showed that increased residual aluminum salts by coagulation-UF pretreatment process by using alum lead to the decreased SWRO membrane salt rejection and flux. As the salt rejection and flux of SWRO membrane decreased, the concentration of silica and residual aluminum decreased. However, when adjusting coagulation pH for coagulation-UF pretreatment process, the residual aluminum salt concentration was decreased and SWRO membrane flux was increased.

위 연구의 목적은 상용화 된 폴리아마이드 기반의 해수담수화 분리막 두 종류를 양쪽성 이온 화합물 중 하나인 MPC를 이용하여 표면 개질을 진행한 후, 내오염성 저감 평가에 대한 고찰이다. 표면 개시 원자 이동 라디칼 중합(SI-ATRP) 반응을 이용하여 표면 개질을 진행하였고, 개질 후 분리막 표면의 물리적, 화학적 특성들의 변화를 여러 분석 방법들을 이용해 분석해봄으로써 MPC가 분리막 표면에 합성이 되었음을 확인하였다. 또한 MPC가 개질 됨에 따라서 친수성이 증가한 표면으로 인하여 Sodium Alginate 와 Bovine Serum Albumin에 대한 두 차례의 내오염성 저감 평가 테스트를 통해서 개질 후 해수조건에서 분리막의 막 오염 현상이 저감 되었음을 확인하였다.

본 연구의 목적은 상용화 된 DOW FILMTECTM과 Toray Chemical Korea Inc.의 폴리아마이드 기반 해수담수화 분리막을 양쪽성 이온의 특성을 지니는 화합물인 SBMA를 이용한 표면 개질 후 성능 및 특성 평가에 대한 고찰이다. 표면개질 방법으로 원자 이동 라디칼 중합(ATRP) 반응을 이용하여 진행하였으며, FT-IR, XPS 및 Contact angle 등의 표면 분석 평가를 통해서 SBMA가 분리막 표면에 합성이 되었음을 확인하였고, 성능 테스트 또한 진행하였다. SBMA가 표면에 개질 되면서 양쪽성 이온의 특성을 통해 분리막은 높아진 친수성으로 개질되기 이전 분리막 대비 해수담수화 시스템 운전시 발생 되는 큰 문제점 중 하나인 막 오염 현상을 개선 시켜 줄 것으로 판단된다.

Scale formation is inevitable problem when seawater is treated by vacuum membrane distillation. The reason is the high concentration of calcium ion(Ca2+), sulfate ion(SO4 2-) and bicarbonate ion(HCO3 -). These ions form calcium sulfate(CaSO4) and calcium carbonate(CaCO3) on the membrane. The scale formed on membrane has to be removed, because the flux can be severely reduced and membrane wetting can be incurred. This study was carried out to investigate scale formation and effectiveness of acid cleaning in vacuum membrane distillation for SWRO brine treatment. It was found that permeate flux gradually declined until volume concentration factor(VCF) reached around 1.55 and membrane wetting started over VCF over 1.6 in the formation of precipitates containing CaSO4 during VMD operation. In contrast, when calcium carbonate formed on membrane, permeate flux was gradually reduced until VCF 3.0. The precipitates containing both CaSO4 and CaCO3 were formed on the membrane surface and in the membrane pore.

본 발표는 45,460 m³/d (10 Million Imperial Gallons per Day (MIGD)) 규모를 가진 한국 최초 및 최대 대규모인 부산 기장 해수담수화 플랜트에 대한 소개이다. 본 플랜트는 2010년부터 건설 되어 2015년 말에는 상업 운전이 시작될 예정이다. 플랜트의 특징으로는 국산화된 다양한 전처 리 기술 (DABF, MF, DMF)의 적용, 대용량 16인치 RO 막 적용, 에너지 소모량을 줄이기 위한 대 용량 8 MIGD RO train의 one module화 이다. 16인치 RO 막은 평균 48%의 high recovery rate 과 14.7 LMH high flux의 성능을 보였으며, 최종 power consumption은 약 3.98 kWh/m³을 기록 하였다.