To study the characteristics of ZTO, which is made using a target mixed ZnO:SnO2= 1:1, the ZnO and SnO2 were analyzed using PL, XRD patterns, and electrical properties. Resulting characteristics were compared with the electrical characteristics of ZnO, SnO2, and ZTO. The electrical characteristics of ZTO were found to improve with increasing of the annealing temperature due to the high degree of crystal structures at high temperature. The crystal structure of SnO2 was also found to increase with increasing temperatures. So, the structure of ZTO was found to be affected by the annealing temperature and the molecules of SnO2; the optical property of ZTO was similar to that of ZnO. Among the ZTO films, ZTO annealed at the highest temperature showed the highest capacitance and Schottky contact.

ZnO와 SnO2에 TiO2를 첨가시킨 ZnO-TiO2와SnO2-TiO2세라믹 복합체를 제작하여 1000ppm 일산화탄소에 대한 감응특성을 조사하였다. 상분석을 위해서 X-선 회절 분석을 하였고, 전자 주사 현미경을 이용해서 시편 파단면의 미세구조를 관찰했다. 일산화탄소 감도는 건조공기 분위기에서 측정한 저항(Rdry air )과 1000ppm 일산화탄소 분위기에서의 저항(Rco )을 측정하여 각각의 저항값의 비로 정의하였다. TiO2첨가에 의한 ZnO의 일산화탄소 감도의 변화는 ZT5의 경우 최대 감도가 약 1.7배 감소하였고, TiO 2첨가에 의한 SnO2의 일산화탄소 최대 감도는 약 2.5배 증가함으로써 비교적 ZnO-TiO2배 증가함으로써 비교적 ZnO-TiO2배 증가함으로써 비교적 ZnO-TiO2복합체 보다는 SnO2- TiO2복합체의 일산화탄소 감응특성이 우수했다.