In this study, analysed the characteristics of power drop and surface damage in solar cell through high temperature and humidity test in the 3 case of EVA(ethylene vinyl acetate) and 2 case ribbon thickness. The solar cells were tested during the 500hr in 85℃ temperature and 85% relative humidity conditions, that excerpted standard of PV Module(KS C IEC-61215). Through the EL(Electroluminescence) shots, specimen's surface have partialy damaged. Before and after high humidity and high temperature test, ribbon thickness 200㎛ EVA1 case power drop rate was 8.463%, EVA2 case was 6.667%, EVA3 case was 6.373%. In the ribbon thickness 250㎛ EVA1 case power drop rate was 6.521%, EVA2 case was 8.517%, EVA3 case was 6.019%. EVA3 case was the lowest power and FF(fill factor) drop rate at the 2 case of ribbon thickness, because EVA3 is laerger than EVA1 and EVA2 in thickness, elongation and tensile strength.

The long quasi-periodic (several tens of seconds) pulsations were observed at. short decimetric wavelength (1.42 and 2.00 GHz). Here, we introduce the features (about bandwidth, periodicity, amplitude and relative amplitude) of these pulsations, then give the discussion about them.