This study investigates the thermal expansion characteristics of hydroxyl-terminated polybutadiene(HTPB) based solid propellants, focusing on batch-to-batch variability and accelerated aging effects. Coefficient of thermal expansion(CTE) measurements were conducted using thermomechanical analyzer(TMA) on samples from different manufacturing batches and specimens aged at various temperatures for different durations. Results indicate variations in CTE values between batches, highlighting the significance of manufacturing process control. Accelerated aging experiments reveal minimal systematic changes in CTE, suggesting stability of thermal expansion properties under short-term thermal stress. The overall distribution of CTE values shows concentration within a specific range, indicating consistency in thermal expansion characteristics. These findings provide insights into the thermal behavior of HTPB-based solid propellants, contributing to improved missile design and lifecycle prediction models.

로켓 추진기관의 해체 시 발생하는 고농도 암모늄 퍼클로레이트(AP)를 액상소각 처리 후 추가로 발생하는 저농도의 AP처리를 위해 NF/RO 멤브레인 공정을 적용하였고, 이때 AP제거 특성에 영향을 미치는 인자를 도출하기 위해 다양한 수리화학적 조건에서 전량여과방식으로 실험을 진행하였다. 고체 추진제에서 추출된 용액을 GC/MS와 FTIR분석을 통해 규산염 계열의 실록산 등을 검출하였으나, 이는 극미량이 포함되어 NF/RO 멤브레인 공정에 큰 영향을 미치지 않는 것으로 판단되었다. 상대적으로 낮은 압력의 운용조건에서는 높은 압력조건과 비교하여, 회수율 증가에 따라 농축된 AP의 삼투압 기작이 투과플럭스에 영향을 미치게 되어 13~17% 가량 플럭스가 감소됨을 확인하였다. 또한 AP의 제거율은 수리화학적 운영조건의 변화(압력 및 교반 속도 등)에 따라 크게 좌우됨을 알 수 있었고, 이 경우 NF와 RO 멤브레인 제거율은 각각 10~70%와 26~87% 가량 크게 달라짐을 확인하였다. 본 논문을 통해 NF/RO 멤브레인 공정을 적용한 AP 제거 기작에서 수리화학적 운영조건의 변화에 따른 농도분극, 멤브레인 선택성 및 삼투압 영향이 중요 지배 기작이었으며, 이는 'NF/RO 멤브레인의 물질이동과 선택성'의 기존 이론적 모델과 부합하였다.