Amorphous agglomerates of carbon nanospheres (CNS) with a diameter range of 10-50 nm were synthesized using the solution combustion method. High-resolution transmission elec-tron microscopy (HRTEM) revealed a densely packed high surface area of SP2-hybridized carbon; however, there were no crystalline structural components, as can be seen from the scanning electron microscopy, HRTEM, X-ray diffraction, Raman spectroscopy, and ther-mal gravimetric analyses. Electrochemical and thermo catalytic decomposition study results show that the material can be used as a potential electrode candidate for the fabrication of energy storage devices and also for the production of free hydrogen if such devices are used in a fluidized bed reactor loaded with the as-prepared CNS as the catalyst bed.

착체증합법 및 연소합성법에 의해 Zn0.994Mn0.006Ga2O4녹색형광체 분말을 합성하였으며, 이들의 분말 및 발광특성을 XRD, SEM, BET, PL 등을 사용하여 조사하였고, 이를 고상반응법에 의하여 합성한 시료와 비교하였다. 착체중합법과 연소합성법에 의해 합성한 시료는 각각 500˚C와 400˚C에서 단일 스피텔 상이 생성되었으며, 이들의 입자크기는 고상반응에 의해 합성된 분말에 비하여 작았다. 한편, 착체중합법에 의하여 합성한 분말의 발광강도는 열처리 온도가 900˚C일 때, 연소합성법에서는 반응온도가 400˚C일 때 각각 최대값을 나타내었다.