In this study, synthetic viscose rayon fabric has been used for preparing activated carbon fabric (ACF), impregnated with different concentrations of H3PO4. The effect of H3PO4 im-pregnation on the weight yield, surface area, pore volume, chemical composition and mor-phology of ACF were studied. Experimental results revealed that both Brunauer-Emmett-Teller surface area and micropore volume increased with increasing H3PO4 concentration; however, the weight yield and microporosity (%) decreased. It was observed that samples impregnated at 70°C (AC-70) give higher yield and higher microporosity as compared to 30°C (AC-30). The average pore size of the ACF also gradually increases from 18.2 to 19 and 16.7 to 20.4 Å for 30°C and 70°C, respectively. The pore size distribution of ACF was also studied. It is also concluded that the finalACF strength is dependent on the concentra-tion of impregnant.

This paper presents an analysis technique considering double-layer concrete and time-dependent diffusion behavior, and the results are compared with those from the previous test results through reverse analysis. Through consideration of time effect, the relative error decreases, which shows more reasonable results. Utilizing the diffusion coefficients from Life365, relative errors increases and it needs deeper penetration depth(e) and lower diffusion coefficient ratio(D1/D2) due to higher diffusion coefficient.