Adsorption characteristics of triadimefon and diniconazole(pesticide) by natural zeolite(CLIN) and several synthetic zeolites were investigated. The synthetic zeolites used in this study were as follows: Faujasite synthesized from coal fly ash(FAUF); Zeolite synthesized from the mixture of FAU and Na-Pl synthesized from the ratio of Cheju scoria 6 to coal fly ash 4 by weight((FAU + Na-Pl)SF); Waste fluid catalytic cracking catalyst(FCCw). The distribution coefficient, KD and Freundlich constant, KF decreased in the following sequence : FCCW>FAUF>(FAU+Na-Pl)SF > CLIN among the zeolites. The distribution coefficient and the adsorption capacity of (FAU + Na-Pl)SF for pesticides were 4.4 and 2.6 times higher for triamefon, and 2.0 and 2.4 times higher for diniconazole than those of CLIN, respectively.

Siliceous mudstones are embedded on a large scale in the Tertiary formations of Pohang area. Some useful zeolites such as NsP, (Na, TMA)P, analcime and hydroxysodalite were synthesized from the siliceous mudstones by treating with the variety of solution, i.e ., NaOH, NaOH+NaCl, NaOH, NaOH+NaAlO2and NaOH+TMAOH at the low-temperature hydrothermal system ranging 60~120℃. Major precursor of zeolites is found as opal-CT in the zeolite-forming reaction. Smectite, which is included in considerable amounts in the mudstone, appears to play a major role of Al-source in the zeolite synthesis. In comparison, chalcedonic quartz and mica are rather insoluble in alkaline solution, and thus, these are observed as major impurities in the reaction products. An addition of NaAlO2to NaOH solution is effective for eliminating these impurities in the reaction procedure, through these are partly dissolved when elevating the reaction temperature, concentration, and time. Phase change from NaP to hydroxysodalite takes place at the NaOH concentrations of 3.0~4.0 M, and the reaction is not sensitive to the temperature shift. NaP is more stable at lower NaOH concentration and higher activity of Na+ whereas analcime is sensitive to the temperature change and stable at higher than 100℃ and 2.0~4.0 M in NaOH concentration. For the pure NaP synthesis without any other products, the treatment of mudstones with 1:1 solution of NaOH and NaAlO 2 turns out to be quite effective. NaP was successfully synthesized together with analcime at 100℃ as well as lower concentrations of NaOH+NaCl solution. In addition, the organic type, (Na, TMA)P was formed together with smectite in the 1:1 solution of NaOH and TMAOH.

화산 유리질 암석인 진주암을 대상으로 60-150˚C의 온도 범위에서 다양한 농도의 알칼리 용액으로 수열 처리하므로서, 유리질 성분의 변질 양상 및 제올라이트의 합성 과정을 폐쇄계의 조건에서 연구하였다. 진주암을 속성 기원 제올라이트의 생성 환경에 해당되는 80˚C 및 pH=8-12의 조건에서 100일간 처리하여도, 양간의 단순 용해 양상이 인지될 뿐 제올라이트는 합성되지 않았다. 여기서 처리 용액의 pH가 증가함에 따라, Si과 Al의 농도는 점진적으로 증가되지만 Si/Al의 농도비는 감소하는 경향을 나타내었다. 진주암을 0.1M 이상의 NaOH 용액으로 수열 처리하여 Na-P, 아날심, 체바자이트, Na-X와 같은 제올라이트를 합성하였다. 대개 100˚C를 경계로 60-100˚C의 온도 범위에서 Na-P, 그리고 100-150˚C에서 아날심이 주로 합성되었다. Na-P의 합성 과정에서 시료에 대한 용액의 혼합 조성비가 낮은 경우(〈10ml/g)에 체바자이트, 그리고 처리 용액의 NaOH 농도가 높을 경우 (〉3M)에 Na-X가 Na-P에 수반되어 생성되는 양상을 볼 수 있다. 제올라이트 합성 과정에 있어서 진주암질 유리의 알칼리 용액에 의한 변질은 화산 유리의 속성 변질에 의한 천연 제올라이트 생성 과정과 같은 용해·변질 반응(incongruent dissolution)의 형식으로 진행되는 것으로 해석된다. 그러나 반응 속도론적인 측면에서 보면, 이 실험으로부터 도출된 제올라이트의 합성 조건들은 화산 유리의 속성 변질에 의한 천연 제올라이트 생성 조건의 해석에 직접 적용될 수 없을 것으로 생각된다.

화산 유리질 암석을 출발 물질로 사용하여 저온 (80℃)에서 수열 처리하여 Na-P Na-X 및 Na-A 제올라이트를 합성하였다. 합성과정은 (1) 유리질 분말 시료와 알칼리 용액과의 용해.변질 반응에 의한 1차적인 Na-P의 합성 방식과 (2) 여기서 잔류된 규산질 모액에 Al(OH)3나 NaAlO2의 수용액을 공급하여 보다 고순도의 Na-P, Na-X 및 Na-A를 효과적으로 합성할 수 있었다. 원암의 암상과 조성은 제올라이트들의 화학 조성과 순도 및 백색도같은 물리적 특성에는 영향을 주지만, 합성된 제올라이트의 광물종을 규제하는 주된 요인은 아닌 것으로 해석된다. 합성된 제올라이트의 광물상은 반응 용액의 pH, Al(OH)4 및 Na+에 대한 농도 조건에 주로 의존되는 경향을 나타낸다. 또한 화산 유리질 암석을 제올라이트 합성원료로 활용하는 데에 있어서 (2)와 같음 합성 방안이 보완적으로 시행되면 그 생산성과 효율성을 제고시킬 수 있을 것으로 여겨진다.