For the selective catalytic reduction of NOx with ammonia (NH3-SCR), a V2O5WO3/TiO2 (VW/nTi) catalyst was prepared using V2O5 and WO3 on a nanodispersed TiO2 (nTi) support by simple impregnation process. The nTi support was dispersed for 0~3 hrs under controlled bead-milling in ethanol. The average particle size (D50) of nTi was reduced from 582 nm to 93 nm depending on the milling time. The NOx activity of these catalysts with maximum temperature shift was influenced by the dispersion of the TiO2. For the V0.5W2/nTi-0h catalyst, prepared with 582 nm nTi-0h before milling, the decomposition temperature with over 94 % NOx conversion had a narrow temperature window, within the range of 365-391 °C. Similarly, the V0.5W2/nTi-2h catalyst, prepared with 107 nm nTi-2h bead-milled for 2hrs, showed a broad temperature window in the range of 358~450 °C. However, the V0.5W2/Ti catalyst (D50 = 2.4 μm, aqueous, without milling) was observed at 325-385 °C. Our results could pave the way for the production of effective NOx decomposition catalysts with a higher temperature range. This approach is also better at facilitating the dispersion on the support material. NH3-TPD, H2-TPR, FT-IR, and XPS were used to investigate the role of nTi in the DeNOx catalyst.

V2O5-TiO2 catalysts were prepared by various methods. V2O5-TiO2 were prepared by sol-gel method with different drying conditions (aerogel and xerogel), and V2O5 supported on TiO2 obtained by sol-gel method with precipitation-deposition method and impregnation method. The performance of the V2O5-TiO2 catalysts was investigated for the selective oxidation of hydrogen sulfide in the stream containing both ammonia and excess water. All the catalysts showed good dispersion of vanadium and they had high H2S conversion with no or little production of sulfur dioxide. The V2O5-TiO2 aerogel catalyst prepared by sol-gel method with drying under super critical condition had the highest surface area which led to better catalytic activity compared to those by other synthesis methods.

V2O5/TiO2 catalyst impregnated ceramic candle filters are in principle, capable of performing shallow-bed dust filtration plus a catalytic reaction, promoted by a catalytic deposited in their inner structure. Pilot-scale V2O5/TiO2 catalyst impregnated ceramic candle filters were prepared, characterized and tested for their activity towards the SCR reaction. The effect on NO conversion of operating temperature, gas hourly space velocity, amount of deposited catalyst, pressure drops and long-term experiment (life of catalytic filter) was determined. The following effects of V2O5/TiO2 catalyst impregnated ceramic candle filters in SCR reaction are observed: (1) It increases the activity and widens the temperature window for SCR. (2) When the content of V2O5 catalyst increases further from 3 to 9wt.%, activity of NO increases. (3) NO conversion at first increases with temperature and then decreases at high temperatures (above 400℃ over), possibly due to the occurrence of the ammonia oxidation reaction.

V2O5/TiO2 catalysts promoted with Mn were prepared and tested for selective catalytic reduction of NOx in NH3. The effects of promoter content, degree of catalyst loading were investigated for NOx activity while changing temperatures, mole ratio, space velocity and O2 concentration. Among the various V2O5 catalysts having different metal loadings, V2O5(1 wt.%) catalyst showed the highest activity(98%) under wide temperature range of 200-250℃. When the V2O5 catalyst was further modified with 5 wt.% Mn as a promoter, the highest activity(90-47%) was obtained over the low temperature windows of 100-200℃. From Mn-V2O5/TiO2, it was found that by addition of 5 wt.% Mn on V2O5/TiO2 catalyst, reduction activity of catalyst was improved, which resulted in the increase of catalytic activity and NOx reduction. According to the results, NOx removal decreased for 10%, but the reaction temperature down to 100℃.