This paper proposes a novel way of fabricating aligned porous Sn by freeze-drying of camphene slurry with stannic oxide (SnO2) coated Sn powders. The SnO2 coated Sn powders were prepared by surface oxidation of the initial and ball-milled Sn powders, as well as heat treatment of tin chloride coated Cu powders. Camphene slurries with 10 vol% solid powders were prepared by mixing at 50 oC with a small amount of oligomeric polyester dispersant. Freezing the slurry was done in a Teflon cylinder attached to a copper bottom plate cooled at −25 oC. Improved dispersion stability of camphene slurry and the homogeneous frozen body was achieved using the oxidized Sn powder at 670 oC in air after ball milling. The porous Sn specimen, prepared by freeze-drying of the camphene slurry with oxidized Sn powder from the heat-treated Sn/tin chloride mixture and sintering at 1100 oC for 1 h in a hydrogen atmosphere, showed large pores of about 200 μm, which were aligned parallel to the camphene growth direction, and small pores in their internal walls. However, 100 μm spherical particles were observed in the bottom part of the specimen due to the melting of the Sn powder during sintering of the green compact.

In this paper, tin-waste resources were pulverized and separated by cut-mill and multi cyclone separator, respectively. After the cut-mill process, more than 98% of the Pb-Sn and Sn-Ag-Cu scraps were recovered, and the by-products consisting of metal and oxide could be reused as solder. The separation of pulverized powders was performed using the minimum fluidization velocity depending on the density of the materials. When the flow rate was 21 L/min (70% blower output), it had the highest separation efficiency.