When there is a significant stripping in asphalt pavement, it is common practice to use a hydrated lime (HL) as an anti-stripping additive (ASA). However, since many asphalt plants do not have facilities for weighing and casting HL, they prefer to use of a liquid-type ASA (LA). Therefore, various brands of LAs which show proper anti-stripping function are currently developed, imported, and marketed in Korea. In addition to the anti-stripping effect, the HL has been known to give a significant age-retarding effect on paved asphalt in the field. Therefore, there was a question about whether or not the LA provides the same anti-aging effect as The HL. This study investigated anti-aging effect of the asphalt mixes which were prepared using both ASAs and short-term aged and long-term aged in the laboratory. The absolute viscosity was measured as an aging index from the binder recovered from the mixes after short-term aging (STA) and long-term aging (LTA) processes. The results showed that there was a significant higher aging found from the LA-added mix than the normal mix without any ASA. On the other hands, the mix with HL showed significantly lower ageing level than the LA-added mix and normal mix. The retardation of age-hardening by using HL was more effectively observed when the STA condition was stronger.

PURPOSES: This study aims to show the difference of the binder aging level in the hot-mix asphalt (HMA) mixture after short-term aging (SA) under different aging conditions, such as mixture temperature and duration in hour. METHODS: Three SA times (i.e., 1 h, 2 h, and 4 h) at two temperatures (i.e., 160℃ and 180℃) were used for the normal mixtures prepared using a PG64-22 asphalt. The field long-term aging (LA) was simulated by applying the same LA procedure (65 h at 110℃) to all compacted specimens, prepared at the air void of 7% using each SA-treated mixture, in a convection oven. The binder aging level was measured in terms of large molecular size by gel-permeation chromatography (GPC) from the mixture and the absolute viscosity (AV) from the recovered binder. The aging levels were evaluated using those two properties after SA and LA, and then compared based on the normal SA (NSA) mixture (1 h at 160℃). The service life reduction caused by SA in various conditions was estimated based on the aging level of the field cores from different locations in various service lives. RESULTS: The results of the laboratory evaluation indicated that the binder of the mixture, which was treated at longer SA time and higher temperature, showed a significantly higher aging level than the NSA mixture. The binder aging level from a longer time, such as 2 h and 4 h SA, or at a higher temperature (180℃), were estimated to be similar to that of the mixtures, which had already been in field service for several years. CONCLUSIONS : The HMA mixture should be produced at a moderate temperature, such as 160℃, and placed within a limited hauling and queuing time to avoid a significant short-term aging of the binder before placement in the field pavement. The SA for a longer time at a higher temperature than the NSA condition was found to be detrimental to the service life of the asphalt pavement.

There are several methods determining an appropriate performance grade of virgin binder, which is re(erred as design binder, in RAP contained bituminous mixture design process. However, difficulties have been experienced in utilizing the methods in the field application in Korea, because SHRP binder test, the key tests to determine a design binder, requires well-trained personnel, high price equipment, and time consuming process. Thus, the study investigated the relationship among the binder aging level, RAP contents, and rheologica1 properties of binder. The study results provide mix designer with a simple method in selecting an appropriate grade of virgin binder.

아스팔트는 노화에 따라 물리적 특성변화가 일어난다. 하지만 같은 수준으로 노화시킨 아스팔트 혼합물들임에도 골재와 결합재 등에 따라 서로 다른 강성이나 취성을 보인다. 이는 노화에 의한 바인더 특성 변화의 차이에 기인한 것인데 이와 같이 혼합물 내에서 바인더의 물리적 특성 변화 차이에 영향을 주는 요인에 대한 연구는 별로 없다. 따라서 본 연구에서는 아스팔트 혼합물의 노화 후추출한 바인더의 물리적 특성을 측정하고 물성 차이에 영향을 미치는 요인을 분석하였다. 폴리머 3종류와 골재 두 종류, 두 가지 입도, 두 종류의 아스팔트를 사용하여 32종류의 혼합물을 제조하고, 이를 장 단기 노화 처리하였다. 각 혼합물의 노화 후 Abson recovery 방법으로 바인더를 추출 회생하고 바인더 물성 시험(침입도, 동점도, 절대점도)을 수행하였다. 이를 SAS를 이용하여 통계 분석하였다. 바인더 시험에서 골재 종류와 폴리머가 노화시 물성변화에 차이를 가져오는 심각한 요인임을 알 수 있었고, 입도는 점도 변화에 큰 영향을 미치는 인자인 것임을 확인할 수 있었다. 본 연구 결과, 혼합물 내의 바인더 물성은 골재 종류, 입도, 개질제의 종류, 바인더의 종류 등의 다양한 요인에 의해 많은 영향을 받는 다는 것을 알 수 있었다.

아스팔트는 노화에 따라 물리적 특성변화가 일어난다. 하지만 같은 수준으로 노화시킨 아스팔트 혼합물들임에도 골재와 결합재 등에 따라 서로 다른 강성이나 취성을 보인다. 이는 노화에 의한 바인더 특성 변화의 차이에 기인한 것인데 이와 같이 혼합물 내에서 바인더의 물리적 특성 변화 차이에 영향을 주는 요인에 대한 연구는 별로 없다. 따라서 본 연구에서는 아스팔트 혼합물의 노화 후추출한 바인더의 물리적 특성을 측정하고 물성 차이에 영향을 미치는 요인을 분석하였다. 폴리머 3종류와 골재 두 종류, 두 가지 입도, 두 종류의 아스팔트를 사용하여 32종류의 혼합물을 제조하고, 이를 장 단기 노화 처리하였다. 각 혼합물의 노화 후 Abson recovery 방법으로 바인더를 추출 회생하고 바인더 물성 시험(침입도, 동점도, 절대점도)을 수행하였다. 이를 SAS를 이용하여 통계 분석하였다. 바인더 시험에서 골재 종류와 폴리머가 노화시 물성변화에 차이를 가져오는 심각한 요인임을 알 수 있었고, 입도는 점도 변화에 큰 영향을 미치는 인자인 것임을 확인할 수 있었다. 본 연구 결과, 혼합물 내의 바인더 물성은 골재 종류, 입도, 개질제의 종류, 바인더의 종류 등의 다양한 요인에 의해 많은 영향을 받는 다는 것을 알 수 있었다.